Springer Series in
OPTICAL SCIENCES Founded by H.K.V. Lotsch
Editor-in-Chief: W.T. Rhodes, Atlanta Editorial Board: A. Adibi, Atlanta T. Asakura, Sapporo T.W. Hänsch, Garching T. Kamiya, Tokyo F. Krausz, Garching B. Monemar, Linköping H. Venghaus, Berlin H. Weber, Berlin H. Weinfurter, Munich
133
Springer Series in
OPTICAL SCIENCES The Springer Series in Optical Sciences, under the leadership of Editor-in-Chief William T. Rhodes, Georgia Institute of Technology, USA, provides an expanding selection of research monographs in all major areas of optics: lasers and quantum optics, ultrafast phenomena, opti-cal spectroscopy techniques, optoelectronics, quantum information, information optics, applied laser technology, industrial applications, and other topics of contemporary interest. With this broad coverage of topics, the series is of use to all research scientists and engineers who need up-to-date reference books. The editors encourage prospective authors to correspond with them in advance of submitting a manuscript. Submission of manuscripts should be made to the Editor-in-Chief or one of the Editors. See also www.springer.com/series/624
Editor-in-Chief William T. Rhodes
Ferenc Krausz
Georgia Institute of Technology School of Electrical and Computer Engineering Atlanta, GA 30332-0250, USA E-mail: [email protected]
Ludwig-Maximilians-Universität München Lehrstuhl für Experimentelle Physik Am Coulombwall 1 85748 Garching, Germany and Max-Planck-Institut für Quantenoptik Hans-Kopfermann-Strass 1 85748 Garching, Germany E-mail: [email protected]
Ali Adibi School of Electrical and Computer Engineering Van Leer Electrical Engineering Building Georgia Institute of Technology 777 Atlantic Drive NW Atlanta, GA 30332-0250, USA E-mail: [email protected]
Editorial Board Toshimitsu Asakura Hokkai-Gakuen University Faculty of Engineering 1-1, Minami-26, Nishi 11, Chuo-ku Sapporo, Hokkaido 064-0926, Japan E-mail: [email protected]
Theodor W. Hänsch
Bo Monemar Department of Physics and Measurement Technology Materials Science Division Linköping University 58183 Linköping, Sweden E-mail: [email protected]
Herbert Venghaus Heinrich-Hertz-Institut für Nachrichtentechnik Berlin GmbH Einsteinufer 37 10587 Berlin, Germany E-mail: [email protected]
Horst Weber
Max-Planck-Institut für Quantenoptik Hans-Kopfermann-Strasse 1 85748 Garching, Germany E-mail: [email protected]
Technische Universität Berlin Optisches Institut Strasse des 17. Juni 135 10623 Berlin, Germany E-mail: [email protected]
Takeshi Kamiya
Harald Weinfurter
Ministry of Education, Culture, Sports Science and Technology National Institution for Academic Degrees 3-29-1 Otsuka, Bunkyo-ku Tokyo 112-0012, Japan E-mail: [email protected]
Ludwig-Maximilians-Universität München Sektion Physik Schellingstrasse 4/III 80799 München, Germany E-mail: harald.weinfurter@physik. uni-muenchen.de
David L. Andrews (Editors)
Zeno Gaburro
Frontiers in Surface Nanophotonics Principles and Applications
David L. Andrews Nanostructures and Photomolecular Systems School of Chemical Sciences University of East Anglia Norwich NR4 7TJ U. K. [email protected]
Zeno Gaburro INFM e Dipart. di Fisica, Universita’ di Trento, via Sommarive 14, I-38050 Povo (TN), Italy [email protected]
Library of Congress Control Number: 2006940404 ISBN-13: 978-0-387-48950-6
e-ISBN-13: 978-0-387-48951-3
Printed on acid-free paper. © 2007 Springer Science+Business Media, LCC All rights reserved. This work may not be translated or copied in whole or in part without the written permission of the publisher (Springer Science+Business Media, LCC, 233 Spring Street, New York, NY 10013, USA), except for brief excerpts in connection with reviews or scholarly analysis. Use in connection with any form of information storage and retrieval, electronic adaptation, computer software, or by similar or dissimilar methodology now known or hereafter developed is forbidden. The use in this publication of trade names, trademarks, service marks, and similar terms, even if they are not identified as such, is not to be taken as an expression of opinion as to whether or not they are subject to proprietary rights. 9 8 7 6 5 4 3 2 1 springer.com
Preface
Surfaces and interfaces of all kinds determine our primary sensory experience of the world we inhabit, and our perception of solidity is very largely based on an interpretation of surface data. In the mind of the scientist, a process of abstraction has led to the familiar modeling of surfaces as two-dimensional boundaries between different parts of otherwise three-dimensional systems. Indeed, such ‘ideal’ interfaces satisfactorily engage with simple macroscopic models to describe mechanical, acoustical or optical phenomena as they appear to human perception. Such connections work because, on the length scale of a meter (and a few orders of magnitude above or below), the various dynamical responses of material systems are dominated by the bulk properties of their components. The reliability of this perspective has been significantly undermined by the advent of nanotechnology. As the reader will find in most introductory presentations, the prefix nano derives from the Greek for ‘dwarf’, and the new usage follows its earlier adoption in quantitative unit terminology to denote a factor 10−9 : indeed, nanotechnology deals with systems where the scale of typical lengths is from one up to some tens of nanometers 1nm = 10−9 meter. To see why this makes a difference to the relationship between surface and bulk properties, it is instructive to reflect on the deeper physical meaning of such a length scale, which corresponds to a typical length of a few atomic bonds.1 This means that in nanomaterials – materials whose dimensions are confined to the nanometer scale – atoms within the ‘bulk’ are never more than a few bond lengths away from an interface of some kind. Consequently it is no longer possible to consider any intrinsic property of such a material as independent from its boundary properties. Moreover, in some sense we could say that in shifting focus from the macro- to the nano-world, we find materials shifting from primarily bulk-like to surface-like attributes, and it is their surface rather than bulk properties that determine system behavior. There is a whole realm of fascinating phenomena associated with surfaces; although they afford stimulating opportunities to creative minds, their understanding it is by no means an easy endeavor: “God created all matter—but the 1 The bond length scale is more appropriately located in the Ångstrom range 1Å = 01nm.
v
vi
Preface
surfaces are the work of the Devil” was Wolfgang Pauli’s reported view. In this book, we touch on a number of recently developed concepts relating to the nanoscale optical and photonic properties of surfaces, without any attempt at completeness. Some of the ideas are still speculative, as in the case of Chapter 1 which addresses the interaction of light with moving interfaces. Such a concept is particularly intriguing in connection with photonic structures where light can be significantly slowed down – and where it is even possible to conceive superluminal effects. Chapter 2 steers the subject matter to topics of already proven practical application, the use of evanescent optical waves for sensing applications. Of course, the device implementation of any form of nanoscale response is ultimately subject to the development of efficient and inexpensive fabrication techniques, to achieve the necessary nanostructures. In Chapter 3, in the context of potential applications in biology, attention focuses on a case in point, porous silicon, which has captured much scientific attention over the last fifteen years and now seems well placed for significant commercial exploitation. A survey of integrated optoelectronic circuits in Chapter 4 puts us back in the context of one of the most relevant field of applications, where optics and nanotechnology are strongly pushing research and development. Metallic nanostructures are also of major interest, especially for phenomena related to surface plasmons (mobile charge oscillations at metallic-dielectric interfaces): Chapter 5 reviews the properties and applications of gold quantum dots. Finally, Chapter 6 concludes with another topic at the adventurous forefront of the subject, concerning the highly unusual optical properties of surfaces fabricated to develop a chiral topography. We belive that the interplay of surface properties and optics will, in the years to come, more and more emerge as a broad but distinctive field of photonics, one that is rich both in its fundamental interest and its potential for creating major applications. We hope, with this book, to stimulate that interest and the creativity in our readers. Zeno Gaburro, Trento David L. Andrews, Norwich February 2007
Contents
Contributors . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
ix
1. Moving Dielectric Interfaces as Photonic Wavelength Converters . . . . . Zeno Gaburro
1
2. Evanescent Waves as Nanoprobes for Surfaces and Interfaces: From Waveguide Technology to Sensor Application . . . . . . . . . . . . . . . . . 19 Silvia Mittler and Bernhard Menges 3. Porous Silicon Electrical and Optical Biosensors . . . . . . . . . . . . . . . . . . . . Huimin Ouyang, Marie Archer, and Philippe M. Fauchet
49
4. Optoelectronic-VLSI: Device Design, Fabrication, and Performance . . . 73 David V. Plant 5. Luminescence of Gold Nanoparticles . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 99 Luca Prodi, Gionata Battistini, Luisa Stella Dolci, Marco Montalti, and Nelsi Zaccheroni 6. Optics of Slanted Chiral STFs . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 129 Fei Wang Index . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 169
vii
Contributors
Zeno Gaburro INFM e Dipart. di Fisica, Universita’di Trento, via Sommarive 14, I-38050 Povo (TN), Italy Silvia Mittler Department of Physics and Astronomy, The University of Western Ontario London, Ontario N6A 3K7, Canada Bernhard Menges Max-Planck-Institut für Polymerforschung, Ackermann Weg 10, 55128 Mainz, Germany Huimin Ouyang Department of Electrical and Computer Engineering and Center for Future Health, University of Rochester, Rochester NY 14627, USA Marie Archer Department of Electrical and Computer Engineering and Center for Future Health and Department of Biomedical Engineering, University of Rochester, Rochester NY 14627, USA and Permanent address: U.S. Naval Research Laboratory, Center for Biomolecular Science and Engineering, Washington D.C. 20375 Philippe M. Fauchet Department of Electrical and Computer Engineering and Center for Future Health and Department of Biomedical Engineering, University of Rochester, Rochester NY 14627, USA David V. Plant Department of Electrical and Computer Engineering, McGill University Luca Prodi Department of Chemistry “G. Ciamician”, University of Bologna via Selmi 2, 40126 Bologna Italy Gionata Battistini Department of Chemistry “G. Ciamician”, University of Bologna via Selmi 2, 40126 Bologna Italy Luisa Stella Dolci Department of Chemistry “G. Ciamician”, University of Bologna via Selmi 2, 40126 Bologna Italy ix
x
Contributors
Marco Montalti Department of Chemistry “G. Ciamician”, University of Bologna via Selmi 2, 40126 Bologna Italy Nelsi Zaccheroni Department of Chemistry “G. Ciamician”, University of Bologna via Selmi 2, 40126 Bologna Italy Fei Wang Micron Technology, Inc. 8000 S. Federal Way. P. O. Box 6 Boise, ID 83707-0006, USA
1 Moving Dielectric Interfaces as Photonic Wavelength Converters Zeno Gaburro University of Trento, Italy [email protected]
1.1 Introduction A distinctive characteristic of optical communications is the ability of parallel transmission and signal processing. To fully exploit this feature, one needs not only tunable light sources and fast detectors, but also complex devices such as add-drop filters, routers, and wavelength converters [1]. Several approaches are possible regarding wavelength conversion [2, 3]. They can be grouped into two classes, as either all-optical or electro-optical techniques. In the former case, optical signals are directly processed and frequency-shifted in the optical domain. All-optical means include for example cross-gain and cross-phase modulation, and four-wave mixing in semiconductor optical amplifiers [3]. The other option is electro-optical techniques, for which signals must be first transformed into electrical signals, processed, and then back transformed into optical signals. The advantage of the second approach stems from the fact that signal processing is conducted inside the electronic domain, which relies on established technologies. The disadvantage is that it clearly requires additional overhead for the optical–electrical–optical (OEO) conversions. Moreover, electrical effects have generally slower time constants than optical effects and thus lower bandwidth available. Technology of electro-optical converters is complex, suggesting significant power consumption and large number of components and costs when a high bit rate is required [2]. It is well known that reflection and refraction by moving interfaces lead to Doppler shift of frequency of the incident waves, and therefore can be proposed as an all-optical solution for wavelength conversion [4, 5]. Compared to other physical effects — including for example the Raman effect — the Doppler shift provides a way to continuously tune photon energies. In this work we show that reflection and refraction by dielectric interfaces in inertial frames can be directly interpreted as photonic phenomena — in the sense that they act on 1
2
Zeno Gaburro
photons — even within a fully classical description. The photon balance at the interface is indeed both conserved and invariant under any inertial motion of the interface. Conservation of photon balance means that if we respectively label as Ni , Nr = r Ni and Nt = t Ni the number of incident, reflected and refracted photons per unit time per unit area (where 0 ≤ r t ≤ 1), then r + t = 1, in any inertial frame. Invariance means that r and t do not depend on the inertial frame. As we show, the values of r and t are the well-known power reflection and refraction coefficients, as calculated in the frame of reference at rest with the interface. Conservation and invariance of photon fluxes stay jointly consistent with the conservation of energy and with Doppler shifts. An interesting option to obtain an interface moving at high speed is to modulate in space and time the dielectric function of the medium without putting it into real motion. This is possible if the materials exhibit a significant electro-optical effect, and if this effect can be driven by an injected electromagnetic wave — for example, by a microwave, as done in traveling wave modulators. We show that conservation and invariance of photon fluxes hold even in this case, in which there is relative uniform motion between the interface and the media.
1.2 Electromagnetic Waves in Inertial Dielectric Media Maxwell’s equations in the SI system of units are [6, 7] · B = 0
×E+
B = 0 t
· D = f
×H−
D = Jf t
(1.1)
where the subscript f refers to free charge and current densities. The first two equations above allow the introduction of potentials and A such that E = − −
A t
B = × A
(1.2)
The effect of bound (or polarization) charges is included in the relationships D = l E
l H = B
(1.3)
where l and l are, respectively, the dielectric and magnetic permittivity of medium l. All media are here taken as nonabsorptive ( l and l are purely real), isotropic (the dielectric and magnetic tensors are scalar lij = l ij , ijl = l ij ), and nondispersive ( l = l , l = l ). This latter condition implies that the phase and group velocity of light coincide, and that the medium response is local in space and time. We will indicate with 0 and 0 the permittivities of vacuum. Equations (1.3), together with J = l E
(1.4)
1. Moving Dielectric Interfaces as Photonic Wavelength Converters
3
are known as constitutive equations, as they express the role of the material. In the following, the medium of incidence will be labeled as medium 1, and the medium of transmission as medium 2. Equations (1.1) and (1.2) hold in any inertial frame of reference, whereas Equations (1.3) and (1.4) are valid only in an inertial frame at rest with the media,1 i.e., they are not covariant [6]. Their general extension to any inertial frame was first derived by Minkowski in 1908 [8]. According to the special theory of relativity, fields E, B, D, and H can be expressed as four-dimensional tensors F and G as ⎡ ⎤ 0 −Ex −Ey −Ez ⎢+Ex 0 −cBz +cBy ⎥ ⎥ F=⎢ ⎣+Ey +cBz 0 −cBx ⎦ +Ez −cBy +cBx 0 (1.5) ⎡ ⎤ 0 −cDx −cDy −cDz ⎢+cDx 0 −Hz +Hy ⎥ ⎥ G=⎢ ⎣+cDy +Hz 0 −Hx ⎦ +cDz −Hy +Hx 0 We label as O the frame of reference of the laboratory, and as O′ the frame of reference stationary with the moving media. Physical quantities are labeled accordingly. The relationships between electromagnetic tensors as expressed in the two different frames are given by F = L′ · F′ · L′T
(1.6)
G = L′ · G′ · L′T
where L′ is the Lorentz transformation matrix O′ → O (the direct transformation O → O′ being labeled as L) [9]: ⎤ ⎡ ⎤ ⎡ −T vx /c ⎦ = ⎣vy /c⎦ = √ 1 2 L = ⎣ (1.7) 1−T · T − I + v /c +1 z L′ = L −1 = L − In the definitions (1.2), I is the three-dimensional identity matrix, and is the √ velocity of frame O′ with respect to O, where c = 1/ 0 0 is the velocity of light in vacuum. The general constitutive relations in the laboratory frame are found by expressing the fields in O′ as functions of the fields in O (by using the direct Lorentz transformations, L), and inserting them into Equations (1.3). The result is D+ 1
× H = l E + c × B c
l H − c × D = B −
× E c
Hereafter, we assume that the frame at rest with the media is inertial.
(1.8)
4
Zeno Gaburro
If Equations (1.8) are plugged into Maxwell’s equations (1.1), a general tensor wave equation is obtained [10], which is valid in any frame in uniform translation with respect to the frame at rest with the media. If no free charges nor free currents are present in the dielectric, by choosing the Coulomb gauge ( · A = 0 and = 0) for the potentials, the general wave equation simplifies as [10]
2 1 1 2 − 2 2 − n2l − 1 2 · + = 0 c t c t (1.9)
2 1 1 2 − 2 2 − n2l − 1 2 · + A = 0 c t c t where we have defined the refractive index as
l l nl =
0 0
(1.10)
The solutions of Equations (1.2) are plane waves. Thus, plane waves are the general solutions of Maxwell’s equations in any inertially moving rigid medium, in the absence of free charges and currents. The dispersion relation of a general solution of Equations (1.2) is [10] k2 −
2 − n2l − 1 2 − · k2 = 0 c2 c
(1.11)
In the frame at rest with the medium, Equations (1.2) reduce to the well-known special case
n2 2 − 2l 2 = 0 c t (1.12)
n2l 2 − 2 2 A = 0 c t with dispersion k2 −
2 n2l = 0 c2
(1.13)
The phase velocity of plane waves which are solutions of Equations (1.12) is vl = c/nl . The medium impedance is defined as [9] l (1.14) l =
l In the following, we shall restrict for simplicity to the case where both the light propagation and the interface motion are in the direction normal to the interface.
1. Moving Dielectric Interfaces as Photonic Wavelength Converters
ωi’,ki’
ωr’,kr’ x O
O z
y Laboratory Frame
5
ωt’,kt’ x’ Interface Frame z’
y’
v
F i g u r e 1.1. Frames of reference.
In Figure 1.1, the frame O′ — the frame of the interface — is at rest with respect to the interface. We set the x′ and y′ axes of O′ to lay in the plane of the interface, and the z′ axis to be perpendicular to the interface. The interface is moving at velocity v = vuz , with v > 0, with respect to the reference frame O. We start by considering in Section 1.3, the standard case of two rigidly moving media of different permittivities ( 12 , 12 ) separated by a flat interface. In this case, which we refer to as the material interface case, the two media are at rest in the interface frame. In Section 1.4, we extend the discussion to the case where the interface is traveling with respect to the media. In this traveling interface case, the media are at rest in the laboratory frame O, but their permittivities are modified in time by a traveling electromagnetic wave via the electro-optical effect which creates an effective interface between regions of different permittivities.
1.3 Material Interface Case For the observer O′ , the case under study is just the classical case of reflection and refraction by the interface between two media at rest. The phase matching condition at any point of the still interface requires that a single plane wave generates a single reflected and a single refracted plane wave, and that frequency is conserved [6, 7, 11]. We label the frequency of any wave as ′ (′ = ′i = ′r = ′t ). The following relationships hold for the k-vectors and phase velocities: ki′ = ′ vph i
′ n c 1 c = n1
kr′ = − ′ vph r
′ n c 1
c =− n1
kt′ = ′ vph t
′ n c 2 c = n2
(1.15)
where the subscripts i r t refer, respectively, to incident, reflected, and refracted plane wave.
6
Zeno Gaburro
The Poynting vectors S′ = E′ × H′ in O′ are S′i = + Si′
′2 Ei′2 ′ ′ ′2 Ei′2 ′ Ei′2 ′ ′ uz Sr = − uz St = + u 1 1 2 z
E ′2 = i 1
Sr′
′2 Ei′2 =− 1
St′
(1.16)
′2 Ei′2 = 2
where we have introduced the symbols ′ and ′ ′ =
Er′
− 1 = 2 Ei′
2 + 1
′ =
Et′ 22 = Ei′
2 + 1
(1.17)
which are, respectively, the reflection and refraction coefficients of the electric fields in the frame O′ . They are obtained by applying the boundary condition (equal tangential components in media 1 and 2) to the electric field E′ and to the magnetic field H′ . The electromagnetic energy density w′ = 1/2 E′ · D′ + B′ · H′ in O′ is, [11] for each wave, wi′ =
Ei′2 c1
wr′ =
′2 Ei′2 c1
wt′ =
2 Ei′2 c2
(1.18)
The conservation of energy at the interface can be expressed as Si′ + Sr′ − St′ = 0
(1.19)
as obtained by substituting Equations (3.1) into Equations (1.16). In Equation (1.19), Si′ and Sr′ are added with positive sign because the z′ axis points from medium 1 toward the interface, whereas St is added with negative sign because the z′ axis points from the interface toward medium 2. Since the Poynting vector and the electromagnetic energy in a nonabsorbing medium are ′ , Equation (1.19) can also be written in the form related by S′ = w′ vph ′ ′ ′ ′ ′ wi′ vph i + wr vph r − wt vph t = 0
(1.20)
We define the photon fluxes as Ni′ =
Si′ S′ S′ Nr′ = r ′ Nt′ = t ′ ′ i r t
(1.21)
This definition has a clear meaning in the context of the quantization of the field, but in this context of classical electrodynamics it is clearly arbitrary. As there is no change in frequency upon reflection and refraction, from Equation (1.19) one also trivially derives the conservation of the number of photons (Figure 1.2) Ni′ + Nr′ − Nt′ = 0
(1.22)
1. Moving Dielectric Interfaces as Photonic Wavelength Converters medium 1
7
medium 2
F i g u r e 1.2. Schematic representation of photon balance in the frame of reference at rest with media. Individual photons are pictorially represented as spheres. If we indicate with Ni′ , Nr′ , and Nt′ the instantaneous fluxes of incoming, reflected, and refracted photons at the interface, we have, for the case in this figure, the ratio ′2 = Nr′ /Ni′ = 2/3 and ′2 1 /2 = Nt′ /Ni′ = 1/3, where ′2 and ′2 1 /2 are the classical power reflection and transmission coefficients. Indeed, the photon balance is equivalent to the classical power balance because of the uniformity of ′ .
The phase matching condition must be satisfied at the interface also in O because the phases are Lorentz invariant. Hence, there is only a single reflected and a single refracted wave also for the moving interface. To calculate the frequencies i , r , and t and the k-vectors ki , kr , and kt , as they are measured by the O observer, we have to transform the 4-vectors which contain the information about ′ and k′ of the three waves from the O′ to the O reference frame, according to the Lorentz transformation. The four-dimensional k′ -vectors are ⎡ ′ ⎤
⎡ ′ ⎤
⎡ ′ ⎤
⎡ i ⎤
⎡ r ⎤
⎡ t ⎤
c
Ki′
c
c
⎢0⎥ ′ ⎢0⎥ ′ ⎢0⎥ ⎢ ⎥ ⎥ ⎢ ⎥ =⎢ ⎣ 0 ⎦ Kr = ⎣ 0 ⎦ Kt = ⎣ 0 ⎦ ki′ kr′ kt′ c
c
(1.23)
c
⎢0⎥ ⎢0⎥ ⎢0⎥ ⎢ ⎥ ⎢ ⎥ ⎥ Ki = ⎢ ⎣ 0 ⎦ Kr = ⎣ 0 ⎦ Kt = ⎣ 0 ⎦ ki kr kt Thus, we have to calculate Ki = L′ · Ki′
Kr = L′ · Kr′
Kt = L′ · Kt′
(1.24)
8
Zeno Gaburro
The two Lorentz matrices, L from O to O′ , and L′ from O′ to O, are ⎡ ⎤ ⎡ ⎤ 0 0 − 0 0 ⎢ 0 10 0 ⎥ ⎢ 0 10 0 ⎥ ⎥ ⎥ L=⎢ L′ = ⎢ (1.25) ⎣ 0 0 1 0 ⎦ ⎣ 0 0 1 0 ⎦ − 0 0 0 0 where we have followed the usual definitions = v/c and = 1/ 1 − 2 . We finally obtain the expressions for the O observer as i = ′ 1 + n1 r = ′ 1 − n1 t = ′ 1 + n2 ki =
′ ′ ′
n1 + kr = − n1 − kt = n2 + c c c
(1.26)
The Doppler shift of the frequency of the reflected and refracted wave is then expressed as r = i
1 − n1 1 + n1
t = i
1 + n2 1 + n1
(1.27)
It is useful to find also the phase velocities of the incident, reflected and refracted waves for the O observer. From the general definition vph = /k it is vph i =
i 1 + n1 =c ki n1 +
vph r =
r 1 − n1 = −c kr n1 −
vph t =
t 1 + n2 =c kt n2 +
(1.28) It is immediate to verify that Equations (1.28) are a particular case of the dispersion shown as Equation (1.11). Equations (1.28) suggest a general definition for the observer O for the “effective” refractive index of a moving medium as nl = c/vph . In general it is − → n + − → nl = l 1 + nl
− → n − ← n−l = l 1 − nl
(1.29)
where nl is the refractive index of the medium at rest, and the left (right) equation applies to the case of phase velocity vph along (opposite to) the medium velocity v. In order to gain physical insight into the expressions of Equations (1.28), it is customary to develop the Taylor expansions of vph to first order in as
c 1 vph i ≃ = +v 1− 2 n1 n1
1 c vph r ≃ = −v 1− 2 (1.30) n1 n1
1 c +v 1− 2 vph t ≃ = n2 n2
1. Moving Dielectric Interfaces as Photonic Wavelength Converters
9
time
where, besides the c/nl term — the “still” medium term appearing also in Equations (1.3) — an additional term appears, which is linear in v, referred to as Fresnel drag. Because of the Fresnel drag, the motion of the medium pulls the light along the direction of the medium velocity v. For example, for positive velocity v in Figure 1.1, the phase velocity of incident and refracted light increases, whereas it decreases for the reflected light. In particular, the Fresnel i.e., when the velocity of the medium drag becomes critical when > n−1 l exceeds the velocity of light in the medium at rest. The sign of frequency and velocity change. While the latter effect is intuitively understandable, the change of sign of frequency has a deeper meaning, which is physically interpreted in the sketch shown in Figure 1.3. We now consider the transformation of the fields. At normal incidence, polarizations of wave are degenerate. If we assume that in O′ E′ is directed as u′x , then the second of Equations (1.1) implies that B′ is directed as u′y , and Equations (1.3) imply that D′ and H′ are also respectively directed as u′x and u′y . The Lorentz transformations (1.2) in the particular case of translational velocity along z — Equations (1.25) — maintain the same directions, respectively, also for E, B, D,
Δx
Δt
E
H
space
F i g u r e 1.3. In this schematic plot, we represent a one-dimensional medium, along the axis of space, as a periodic lattice of circles (only three circles are shown for simplicity). The circles are colored differently to help track their position in time. The effect of medium on light propagation, which is described by its refractive index nl , is represented in a simplified way as a process of successive absorptions and reemissions of light photons. We assume that the process reproduces itself periodically in time. In a period t, an emission, a travel to the adjacent (moving) lattice site, and an absorption happen. For > n−1 l , the velocity of moving medium is larger than the phase velocity of light. In the figure, we consider this condition with the light counterpropagating with respect to the medium. The figure shows that the sign of Poynting vector S does not agree with the sign of the group velocity of the perturbation (which in the present nondispersive medium coincides with the phase velocity). Since S = w vph holds, where w is the energy density (1.33) and vph is the velocity of the wave (1.28), this also explains the negative sign of the energy density w.
10
Zeno Gaburro
and H. The transformed field components in O are Ei = Ei′ 1 + n1 Er = ′ Ei′ 1 − n1 Et = ′ Ei′ 1 + n2 Bi =
′ Ei′ ′ Ei′ Ei′
+ n1 Br =
− n1 Bt =
+ n2 c c c
Di =
Ei′ ′ Ei′ ′ Ei′
n1 + Dr =
n1 − Dt =
n2 + c1 c1 c2
Hi =
′ Ei′ ′ Ei′ Ei′
n1 + 1 Hr =
n1 − 1 Ht =
n2 + 1 1 1 2
(1.31)
where Ei′ is the electric field in the reference frame O′ . From Equations (1.31), two general results should be pointed out. First, the ratio E/H = for any plane wave does not depend on the state of motion of the dielectric. This is not trivially expected from the Lorenz transformation: for example, the ratio E/B does depend on the state of motion. Second, since −1 < < 1, the two fields B and D never change sign, but the fields E and H do: this happens for waves traveling in the opposite direction to the translation of the medium, in the critical condition ( > n−1 l ). In Equations (1.31) we have only calculated the magnitude of the fields. The Poynting vector S = E × H in O is Si = +
2 Ei′2
1 + n1 2 uz 1
Sr = −
2 ′2 Ei′2
1 − n1 2 uz 1
St = +
2 ′2 Ei′2
1 + n2 2 uz 2
(1.32)
The sign of the Poynting vector is invariant for any value of because the change of sign in the critical condition > n−1 occurs simultaneously for E l and H. The electromagnetic energy density w = 1/2 E · D + B · H in O is wi =
2 Ei′2
1 + n1 n1 + c1
wr =
2 ′2 Ei′2
1 − n1 n1 − c1
wt =
2 ′2 Ei′2
1 + n2 n2 + c2
(1.33)
1. Moving Dielectric Interfaces as Photonic Wavelength Converters
11
where we notice that in critical condition > n−1 l the energy density becomes negative, but the relationship S = wvph still holds, as for media at rest. We provide an interpretation of the result of negative energy in Figure 1.3. In the laboratory frame, to prove the conservation of energy, one must take into account the mechanical energy which is transferred to the material system by the electromagnetic pressure applied by the waves to the interface. The momentum density (momentum per unit volume) g carried by the plane wave is [11] g = D×B =
S 2 vph
(1.34)
where the last equality is a consequence of the relationships D = E/vph and B = H/vph , which hold for any state of inertial motion, as directly derived from Equations (1.31). The mechanical power performed by the electromagnetic wave on the interface per unit area is W = g·v
(1.35)
diminished by the momentum per unit time per unit area stored in the space created by the interface motion (gv). Since g and S are related by Equation (1.34), one can show that the mechanical energy flux is equal to the excess energy per unit time per unit area E injected to the interface by the electromagnetic waves, which is the balance of Poynting vectors of the waves, diminished by the energy per unit time per unit area stored in the space created by the interface motion: E ′ = wi vphi − c + wr vphr − c − wt vpht − c =
′2 Ei′2 ′2 Ei′2 Ei′2
1 + n1 −
1 − n1 −
1 + n2 = 0 1 1 2
(1.36)
The last line of Equation (1.36), when compared to Equations (1.33) and (1.3), suggests to repeat the calculation for the photon flux instead of the energy flux. We must divide the terms of Equation (1.36) by , where is the respective frequency of each term, as calculated by Equations (1.3). Thus, we calculate the photon balance as the difference N between the incoming and outgoing photon fluxes of the waves, diminished by the stored photons in the space created by the interface motion: w w w N = i vphi − c + r vphr − c − t vpht − c i r t Ei′2 1 + n1 ′2 Ei′2 1 − n1 ′2 Ei′2 1 + n2 − − ′ 1 1 + n1 ′ 1 1 − n1 ′ 2 1 + n2
′2 ′2 1 E ′2 − − = 0 (1.37) = i ′ 1 1 2 =
where we have made use of Equation (1.19). The interpretation of this last interesting result is that the interface between the two dielectrics acts as a
12
Zeno Gaburro medium 1
medium 2
F i g u r e 1.4. Schematic representation of photon balance in a frame of reference O in motion with respect to the frame O′ of media (axis conventions are given in Figure 1.1). The interface moves with velocity vuz in O as indicated by the arrow. Individual photons are pictorially represented as spheres. The ratios of instantaneous fluxes of photons — reflected versus incoming and refracted versus incoming — at the interface (i.e., inside the dashed circle) are invariant with respect to the status of motion (assumed inertial), and are equal to the power reflection and transmission coefficients ′2 and ′2 1 /2 as calculated in the frame at rest with the interface. In this example, ′2 = 2/3 and ′2 1 /2 = 1/3. The interpretation of this interesting result is that the interface between the two dielectrics acts as a number-conserving and invariant photon converter, regardless of its state of (inertial) motion. This joint invariance and conservation law is fully contained inside classical electrodynamics.
number-conserving and invariant photon converter, regardless of its state of (inertial) motion, in quantitative consistency with both Doppler shifts and the conservation of energy. This joint invariance and conservation law is fully contained inside classical electrodynamics. The interpretation is schematically shown in Figure 1.4.
1.4 Traveling Interface Case The physical configuration discussed in this section is schematically represented in Figure 1.5: the media are at rest in the frame O and the electromagnetically created interface is moving at a velocity v in the z-direction. On the other hand, the interface is at rest in the frame O′ . Since the media are now in motion with z-velocity −v with respect to O′ , the calculation of frequency and k-vectors can be carried on as in the previous paragraphs, provided that we use the effective refractive index — as defined in Equations (1.29) — instead of the index of the medium at rest. The frequency is still conserved because the phase matching condition still applies (it depends on the motion condition of the interface only, which is at
1. Moving Dielectric Interfaces as Photonic Wavelength Converters
13
Z
V F i g u r e 1.5. Schematic representation of a traveling wave refractor. Light travels in a waveguide, whose core exhibits some electro-optic effect. The electro-optic effect is controlled by two side electrodes, which are terminated at the end side by a suitable impedance Z. For example, if Z matches the characteristic impedance of the electrode line, the traveling signal exhibits no reflection at Z. The driving signal is provided by a microwave generator V connected between the other sides of the electrodes, which inject a driving signal for the electro-optic effect. The wavefront of the microwave (dashed line) represents a moving interface between two portions of the medium, each with different refractive index. Hence, it can be viewed as an interface in relative motion with respect to two effective media. In order to focus on the effect of motion only, we make the simplifying assumption that the refractive index is everywhere constant in the core, except at the microwave interface, where it exhibits a discontinuity.
rest). Thus, it is again ′i = ′r = ′t = ′ as in Section (1.3). All the equations of Section (1.3) that depend on the index of refraction must now be modified. Equations (1.3) must be replaced by ki′ =
′ n 1 − c 1 − n1
1 − n1 ′ vphi =c n1 −
kr′ = − ′ vphr
′ n1 + c 1 + n1
1 + n1 = −c n1 +
kt =
′ n 2 − c 1 − n2
1 − n2 ′ vpht =c n2 −
(1.38)
−1 We assume that ≤ n−1 1 and ≤ n2 . This assumption means that the interface is traveling at slower velocity than any phase velocity. We do not consider here
14
Zeno Gaburro
different conditions, which require careful discussion beyond the scope of this work. The expressions of the Poynting vectors (1.16) are left unchanged because the general relationship E/H = is invariant with respect to the state of motion of the dielectric. This only means that it is possible to express the magnitude of Poynting vector of a plane wave as E 2 / independently of the state of motion: the magnitude itself is not invariant and depends on the state of motion as calculated in Equations (1.31). The expressions of the reflection and transmission coefficients (3.1) are also based on E/H = and remain unchanged. The electromagnetic energy density w′ = 1/2 E′ · D′ + B′ · H′ in O′ is, for each wave, wi′ =
Ei′2 1 − n1 c1 n1 −
wr′ =
′2 Ei2 1 + n1 c1 n1 +
wt′ =
′2 Ei2 1 − n2 (1.39) c2 n2 −
The conservation of energy can be expressed as in Equations (1.19) and (1.20) and the conservation of photon flux also holds, as in Equation (1.22). The expressions of frequency and k-vectors for the O observer are i = ′ 1 + r =
n1 − 1 − 2 ′ 1 = ′ = 1 − n1 1 − n1 1 − n1
1 ′
1 + n1
ki =
t =
1 ′
1 − n2
′ n1 − 1 ′ n1 1 − 2 ′ n1
+ = = c 1 − n1 c 1 − n1 c 1 − n1
kr = −
′ n 1 1
c 1 + n1
kt =
1 ′ n2
c 1 − n2
(1.40)
If we now calculate the phase velocity (vph = /k), we find vphi =
i c = ki n1
vphr =
r c =− kr n1
vpht =
t c = kt n2
(1.41)
consistent with the fact that the media are still for the observer O. The Doppler shift of the frequency of the reflected and refracted wave is then expressed as r = i
1 − n1 1 + n1
t = i
1 − n1 1 − n2
(1.42)
where it is interesting to note that the Doppler shift of the reflected wave is unchanged with respect to Equation (1.27), but the shift of the transmitted wave is different.
1. Moving Dielectric Interfaces as Photonic Wavelength Converters
15
The transformed field components in O are
Ei = Bi = Di = Hi =
1 Ei′ 1 − n1
n1 Ei′ c 1 − n1
Er =
Br = −
Ei′ n1 1 c 1 − n1 Ei′ 1 1 1 − n1
′ Ei′ 1 1 + n1
Dr =
′ Ei′ n1 c 1 + n1
′ Ei′ n1 1 c 1 + n1
Hr = −
′ Ei′ 1 1 1 + n1
Et = Bt = Dt = Ht =
′ Ei′ 1 1 − n2
′ Ei′ n2 c 1 − n2
′ Ei′ n2 2 c 1 − n2
′ Ei′ 1 2 1 − n2
(1.43)
where the symbols ′ and ′ are, as already stated, unchanged from Equations (3.1). The Poynting vectors S = E × H in O are
Si = +
Ei′2
1 − n1 −2 uz 2 1
Sr = −
′2 Ei′2
1 + n1 −2 uz 2 1
St = +
′2 Ei′2
1 − n2 −2 uz 2 2
(1.44)
The electromagnetic energy density w = 1/2 E · D + B · H in O is
wi =
Ei′2 n1
1 − n1 −2 c 2 1
wr =
′2 Ei′2 n1
1 + n1 −2 c 2 1
wt =
′2 Ei′2 n2
1 − n2 −2 c 2 2
(1.45)
−1 Even though we have limited the analysis to ≤ n−1 1 and ≤ n2 , we mention that the energy density as resulting from Equations (1.45) does not become negative under any condition, consistent with the fact that media are at rest in the observer frame.
16
Zeno Gaburro
Following the same reasoning as in Section 1.3, we now obtain, in place of Equation (1.37), N =
w w wi
v − c + r vphr − c − t vpht − c i phi r t
′2 Ei′2 1 + n1 2 ′2 Ei′2 1 − n2 2 Ei′2 1 − n1 2 − − ′ 1 1 − n1 2 ′ 1 1 + n1 2 ′ 2 1 − n2 2
′2 ′2 1 Ei′2 − − = 0 (1.46) = ′ 1 1 2 =
Because of Equation (1.19), the joint invariance and conservation law N = 0 illustrated in Figure 1.4 is valid also for this case. Also in this traveling interface case, there is a sizable Doppler shift (1.42) of both the reflected and the transmitted waves.
1.5 Conclusions In this chapter we have discussed some interesting consequences of Maxwell’s equations in moving media: the moving interface between two inertial dielectrics acts as a number-conserving and invariant photon converter. Although the calculations have been performed using classical electrodynamics, the results have a clear interpretation in terms of conservation of number of energy quanta if the photon flux is calculated by dividing the classical power fluxes of incident, reflected, and refracted waves by the quantities irt , where is the reduced Planck constant and irt are the corresponding, Doppler shifted, frequencies. Two cases have been considered: the standard, material interface one, where the two media are rigidly moving in the laboratory frame, and a novel, traveling interface one, where the medium is at rest, and the interface is created by a traveling electromagnetic pulse via the electro-optic effect. The Doppler shifts of the reflected and the transmitted waves have been calculated for the two cases: while the shifts of the reflected wave are the same in the two cases, those of the transmitted wave differ. As it does not require mechanical objects moving at relativistic speed, the traveling interface system appears as most suited to produce large wavelength shifts. From the point of view of basic physics, it appears as very promising in view of studies of interfaces at ultrarelativistic speeds, where the interface velocity is larger than the phase and group velocities in the media. This regime is very interesting as it opens the way toward experimental studies of optical black holes, and of the related quantum effects. Acknowledgments. The help of L. Pavesi, F. Riboli, A. Recati, I. Carusotto, S. Prezioso, and M. Ghulinyan is acknowledged.
1. Moving Dielectric Interfaces as Photonic Wavelength Converters
17
References 1. L. Pavesi and D. J. Lockwood, Silicon Photonics, Springer, Berlin (2004). 2. T. Durhuus, B. Mikkelsen, C. Joergensen, S. L. Danielsen, and K. E. Stubkjaer, J. Lightwave Technol. 14, 942–953 (1996). 3. S. J. B. Yoo, J. Lightwave Technol. 14, 955–966 (1996). 4. M. Lampe, E. Ott, and J. H. Walker, Phys. Fluids 21, 42–54 (1989). 5. I. Scherbatko, Opt. Quantum Electron. 31, 965–979 (1999). 6. A. Sommerfeld, Electrodynamics, Academic Press, New York (1952). 7. J. D. Jackson, Classical Electrodynamics, Wiley, New York (1962). 8. H. Minkowski, Göttinger Nachr., p. 53 (1908). 9. S. J. Orfanidis, Electromagnetic Waves and Antennas. www.ece.rutgers.edu/ orfanidi/ ewa, 2004. 10. J. M. Saca, J. Mod. Opt. 36, 1367–1376 (1989). 11. W. Greiner, Classical Electrodynamics, Springer, Berlin (1998).
2 Evanescent Waves as Nanoprobes for Surfaces and Interfaces: From Waveguide Technology to Sensor Application Silvia Mittler1 and Bernhard Menges2 1
Department of Physics and Astronomy, The University of Western Ontario, London, Ontario N6A 3K7, Canada [email protected] 2 Max-Planck-Institut für Polymerforschung, Ackermann Weg 10, 55128 Mainz, Germany
2.1 Introduction This chapter does not deal with a system which is nanoscopic in all three dimensions of space. A classical nano-object with nanoscopic dimensions in all three dimensions would be, for instance, a nanoparticle which can exhibit quantum effects due to its size. In the case of an evanescent wave at a surface of an optical waveguide we deal with a nanoscopic effect in one dimension only: perpendicular to the propagation direction of the electromagnetic wave. Both other dimensions are macroscopic and in the theory typically treated as infinite. But because of this seminanoscopic circumstance at an “optical surface” we speak about Surface Nanophotonics. The future will definitely show how these one-dimensional nanodevices can be combined with two- or three-dimensional nanostructures to foster new physical effects and new applications.
2.2 Waveguides An optical waveguide is in principle a very simple structure. In its simplest form it consists of one sheet of transparent dielectric material with a thickness in the range of a micrometer. Because it is surrounded by air having a refractive index nair = 1, light propagating in the thin layer of the dielectric material 19
20
Silvia Mittler and Bernhard Menges
with a refractive index larger than 1 [n(waveguide dielectric material) > 1] can experience total internal reflection at the dielectric–air interface when it is incident above the critical angle of total internal reflection critical sin critical = nair/nwaveguide dielectric material [1–3]. When the light faces this total internal reflection on both sides of the dielectric sheet, the light is trapped and can only propagate by zigzagging between both interfaces within and along the sheet (Figure 2.1a). It is then called a guided wave or beam and the dielectric sheet an optical waveguide. Not all angles above the critical angle of total internal reflection will lead to an efficient guiding of the light. Only certain angles of reflection can lead to an efficient propagation of the light along the guide which leads to constructive interference. Therefore, a mode structure exists with specific angles of reflection. If we have a closer look at the dielectric–air interface when light is reflected there totally, we find that with every reflection the beam experiences an offset (a little shift in position toward the main propagation direction), called the Goos-Hänchen shift [1, 4–7]. This shift occurs because the total reflection is not happening completely at the dielectric–air interface, but partly in the air. Outside of the dielectric sheet a “film of light” decaying exponentially away in intensity from the interface is found. This is called the evanescent field. If one treats this three-layer problem (air–dielectric transparent sheet–air) with electromagnetic theory, Maxwell’s equations lead in combination with the boundary conditions at both interfaces to two wave equations, one for each polarization direction (s- and p-polarized) and their solutions describe standing z cladding, nc
y
waveguide, nw a
x
substrate, ns
nw > ns, nc cladding, nc waveguide, nw b substrate, ns
TE0
TE1
TE2
F i g u r e 2.1. (a) Asymmetric three layer waveguide architecture with the total internally reflected beam zigzagging along the waveguide. The Goos-Hänchen shift is denoted by the intrusion of the beam into the surrounding materials. (b) Here the field distributions of the first three s-polarized modes are shown. The numbering of the modes is in accordance with their appearing by increasing the waveguide thickness. The index number also signifies the number of zero-field crossings in the field distribution.
2. Evanescent Waves as Nanoprobes
21
waves across the dielectric sheet [4–9]. Depending on the refractive index of the dielectric material and the thickness of the dielectric sheet, various standing wave solutions can be found, all of them showing an oscillating field distribution within the dielectric sheet and evanescent fields on both sides outside the structure (Figure 2.1b). These various solutions are the modes, mentioned above as belonging to specific angles of reflection. In the symmetric case the field distribution is symmetric. Each of these modes has a characteristic wave vector m which is aligned parallel to the waveguide sheet and points into the propagation direction. The effective refractive index Nm for each mode is related to the wave vector by: m = 2 Nm / , with the wavelength of the propagating light. In practice it is difficult to handle sheets of micrometer thickness, so-called free-standing waveguides. Therefore, the dielectric waveguide material is usually located on top of a substrate. In order to keep the condition of total internal reflection in the guide, the substrate needs to have a lower refractive index than the waveguide. Such a structure is called a slab waveguide. The field distribution here is asymmetric because of the asymmetric refractive index distribution. Figure 2.1 shows such an asymmetric waveguide structure with a possible zigzag path including the Goos-Hänchen shift in panel a and the theoretically calculated field distribution for three modes in panel b. Alternative geometries are the fiber optical guides with a cylindrical geometry, trapping the light into a cylinder, basically a channel, where total internal reflection happens in “two” dimensions, confining the beam laterally into the cylinder (Figure 2.2). This kind of stripe or channel waveguides can also be defined in slab waveguides if a lateral refractive index distribution is present,
channel waveguides
fiber embedded channel waveguide
core cladding strip loaded waveguide
slab waveguide cladding planar waveguide
buried waveguide
substrate
F i g u r e 2.2. (Left) The two fundamental waveguide geometries: the fiber and the planar slab waveguide. (Right) Three types of channel waveguides: embedded channel waveguide, strip loaded waveguide, and buried waveguide.
22
Silvia Mittler and Bernhard Menges
allowing total internal reflection of the light back into the stripe from two sides, in addition to the top–bottom confinement of the dielectric sheet itself: a high refractive index material in stripe form embedded in a low refractive index material. Figure 2.2 shows some typical waveguide geometries: the fiber, the slab waveguide, and three classes of channel waveguides. These channel waveguides now allow for various integrated optical devices; light can be distributed from one channel into two or more channels (a device called a splitter), or combined from two channels into one. To summarize: a waveguide is a thin film with a “high” refractive index located on a “low” refractive index substrate guiding light in the form of modes with specific field distributions in two possible polarization directions (s-polarization leads to TE modes and p-polarization to TM modes), always showing an evanescent field outside the structure. Many applications of waveguides are in telecommunications, where the guides are used to bring information in the form of modulated intensities or light pulses to specific targets. Long-distance communication is usually achieved with the use of optical fibers, whereas signal distribution is performed by integrated optical channel waveguides. In all of these applications the guiding effect itself is used [10–12]. In the field of integrated optical sensors, it is not the guiding effect itself that is used, but interactions in the evanescent field present on the surface of the device, or changes in the optical constants within the waveguide material leading to changes in the field distribution. In order to understand how these changes—in the evanescent field or the waveguide itself—can be identified, we discuss how the light can be launched into such thin film structures. Here, basically two classical techniques are available: (1) methods which couple the light by matching the wave vector k of the incident light with the wave vector m of a waveguide mode, and (2) coupling by matching the spatial distribution of the incoming light beam to that of the waveguide mode. Figure 2.3a explains the operation of a grating coupler where the wave vector m of the mth mode is matched by adding or subtracting integer multiples n of the grating vector G; the latter is oriented perpendicular to the grating lines and has a length G = 2 / , with the grating spacing. The experimentally available parameter to adjust for resonant coupling is then the angle of incidence . The prism coupler in Figure 2.3b matches the wave vector of the incoming light with the guided mode wave vector m by increasing it with the help of the higher refractive index of the prism material np in comparison to air. In Figure 2.3c, the light is coupled by focusing it onto the polished endface of a waveguide to match the lateral field distribution. Here no simple experimental selectivity for specific modes is possible, because no experimental adjustment parameter is available. Figure 2.4 shows the scheme of the experimental setup for waveguide characterization. A laser beam at a given wavelength is incident on a coupling grating. The transmitted intensity behind the waveguide is monitored while the angle of
2. Evanescent Waves as Nanoprobes
Efficient coupling can be achieved only under wave vector matching conditions:
θ grating coupler
23
•
a
βm = kph sin θ + - n G G = 2π/Λ
θ prism coupler
b
βm = np khp sin θ
end-fire coupling
c
Matching the spatial distribution of the incident field to that of the guided mode
F i g u r e 2.3. The three classical coupling techniques: (a) grating coupler, (b) prism coupler, (c) end-fire coupling.
incidence is scanned. Each successfully coupled mode is found as an intensity dip in the intensity – angle of incidence scan, because when the light is coupled to the waveguide, it is missing in transmission. The highest resonance angle found is always the 0th mode. In the left-hand corner the thickness and refractive index information is given for that particular mode spectrum at = 6328 nm. The resonance angles m are taken from such a mode spectrum and converted into the effective refractive indices Nm for the various modes:
In the case of grating coupling Nm = nair sin m ± n In the case of prism coupling Nm = sinm cos + np 2 − sin2 m sin with the prism angle (see Figure 2.3). As long as at least two modes are found and the optical data of the substrate are known, the thickness and the refractive index of the waveguide material can be obtained with the help of the effective refractive indices of the modes and an iterative computer routine based on a procedure proposed by Ulrich and Torge in 1973 [13–15]. Because two polarization directions can be used independently to characterize the waveguide, anisotropic refractive indices, arising from anisotropic waveguide fabrication processes, can easily be detected. The simplest form of sensor then involves monitoring changes in the thickness or the refractive indices in the waveguide itself due to any physical or chemical treatment, such as photobleaching, aging, milling, wear, or swelling, (see example below).
24
Silvia Mittler and Bernhard Menges
refractive index and thickness profile 1 1.5
n
substrate waveguide
0
m=1
m=2
m=0
air
1300nm d Θ
laser
1.0 intensity [a.u.]
polarization optics
0.8 0.6 TE2 0.4 0.2
TE1
TE0 0.0 48 50 52 54 56 58 60 62 64 66 68 angle θ [°]
F i g u r e 2.4. Measurement scheme for waveguide characterization with respect to waveguide refractive index and waveguide thickness in s- and p-polarization. The angle of incidence is scanned and the transmitted intensity of a laser incident on the grating is monitored. If a resonance angle is approached the laser beam is coupling into the waveguide structure, so that the light is missing in transmission. Therefore, resonance dips are found in the intensity–angle of incidence scan. The inset shows the waveguide architecture with respect to thicknesses and refractive indices.
The materials used for these kinds of structures vary from classical glasses, engineered glasses, or semiconductors all the way to organic materials, such as polymers, and combinations thereof. Fabrication technologies are also spread along a huge variety of deposition or material modification methods. Two strategies are followed for waveguide fabrication: the deposition of the waveguide material on top of a transparent substrate or the enhancement of the refractive index in a substrate. The deposition techniques include simple approaches like spin coating (polymers and solgel systems) [16–18] timeconsuming methods like Langmuir-Blodgett (LB) film transfer (small organic molecules or polymers leading to intrinsic order) [19–22], extruding (insoluble polymers) [23, 24], and highly sophisticated CVD processes (glasses and semiconductors) [25–28]. The material alteration methods rely on the implantation or exchange of ions with a high polarizability to enhance the refractive index in the material [29]. Typical methods are ion exchange [30, 31] and ion implantation [32]. In all of these technologies one aim is to fabricate waveguides with low intrinsic losses. The waveguide losses are due to electronic absorptions of the material and scattering losses. Therefore, not all materials are suitable for all
2. Evanescent Waves as Nanoprobes
25
optical wavelengths. The regime of transparency dictates the possible operational wavelengths. Scattering can occur on the surface due to roughness, and internally in the waveguide due to refractive index fluctuations such as grain boundaries or orientation fluctuations. Therefore, the waveguide material should be perfectly glassy or alternatively a single crystal [33–35]. The evanescent field is used in integrated optics sensor technology as described by Figure 2.5. A well characterized waveguide is used as a substrate for an adlayer. In the first approximation, let us consider the adlayer as the material to be detected and the waveguide completely characterized. The asymmetric three-layer system becomes a four-layer system, still with two unknowns: the thickness and the refractive index of the adlayer. This more complicated structure as well as five-layer and multilayer structures are theoretically treated in various books [4, 14]. Typically a matrix formalism based on the Fresnel equations [4, 14, 36] is used to calculate the field contributions reflected and refracted at each interface. As seen in Figure 2.5, the adsorption of the adlayer leads to a shift of a waveguide mode to a higher resonance angle, leading to an enhanced effective refractive index N of that mode. The sensitivity S of such a waveguide sensor can be defined as the change in effective refractive index of the mode N with thickness increment d of the adlayer at a fixed refractive index: S = N . It d turns out theoretically and experimentally that this sensitivity S is a function refractive index and thickness profile 2.2 n 1.5 substrate
waveguide
0 160 mn
adlayer Θ
d
1.0
laser
intensity [a.u.]
polarisation optics
0.8 0.6 0.4 0.2
mode shift
0.0 47 48 49 50 51 52 53 54 55 56 57 angle θ [°]
F i g u r e 2.5. A well-characterized waveguide carries an additional adlayer. Due to the adlayer the waveguide mode resonant coupling angle is shifted to a higher angle of incidence. The inset shows the waveguide architecture with respect to thicknesses and refractive indices.
26
Silvia Mittler and Bernhard Menges
of the refractive index contrast n = n(waveguide)-n(medium on top) of the waveguide and the medium on top, as well as on the thickness of the actual waveguide [37, 38]. Figure 2.6 shows the calculated sensitivity S for an asymmetric Ta2 O5 waveguide having a refractive index of 2.2, with an adlayer at n = 15 at 632.8 nm, with increasing waveguide thickness. First, one sees that a minimum waveguide thickness is required for the TE and TM modes to exist in this asymmetric structure. This minimum thickness is called the cutoff thickness. The cutoff thickness is smaller for the TE mode than the TM mode at a given mode number and increases with increasing mode number. The sensitivity maxima are always found very close to the cutoff thicknesses and the sensitivity peak heights decrease with increasing mode number or waveguide thickness, respectively. The sensor designer has to make a choice on how to design a sensor: (1) use a waveguide with maximal possible sensitivity S right there where the TE0 mode shows a sensitivity peak and no other mode exists, losing the possibility to have access to an independent identification of refractive index n and thickness of the adlayer d, or (2) choose a compromise, the highest combination of sensitivities with two modes, e.g., where the TE1 - and TM1 -mode sensitivity lines are crossing, allowing for n and d determination, but losing about a third in sensitivity. The decision has to be governed by the application of the device: if one needs to detect with the highest sensitivity whether a specific molecule is present in a solution and builds up an adlayer or not, sensitivity is the attribute to go for. If a new surface binding strategy is developed, where surface information such as the bonding density and final thickness of the adlayer are required, the compromise solution with two waveguide modes is adequate. Concentration information can also be found in the high-sensitivity case by calibrating the device, which basically serves as the second measurement necessary to gain information about a second variable. 1.6
TE0- mode TE1- mode TM0- mode TM1- mode
δNeff/δda [10-3/nm]
1.4 1.2 1.0
refractive index and thickness profile 2.2 n 1.5
0.8 0.6 0
0.4 0.2 0.0
d 0
100
200
300
400
500
waveguide thickness [nm]
F i g u r e 2.6. The sensitivity S = N/d in 10−3 per nm adlayer is plotted for the first two TE and TM modes with respect to the thickness of a waveguide fabricated out of Ta2 O5 having a refractive index of 2.2 at 632.8 nm. The adlayer is modeled with a refractive index of 1.5. The inset shows the waveguide architecture with respect to thicknesses and refractive indices.
2. Evanescent Waves as Nanoprobes personal computer
27
I
lock-in Θ
0
chopper Θ
stepmotor
laser
polarisation optics
waveguide chip goniometer photo detector
F i g u r e 2.7. Experimental setup for the determination of the coupling angles.
Figure 2.7 shows the principle for a grating coupling measurement. The waveguide sample carrying a coupling grating is rotated on a goniometer, systematically changing the angle of incidence from a chopped laser with adjusted polarization. Detectors at the ends of the waveguide structure detect the modes as peaks, when light is coupled and guided to them. For sensor purposes the waveguide is connected to a cuvette with a liquid or gas handling system allowing liquids or gases to reach the waveguide surface and build up an adlayer. A lock-in technique is used to maximize the signal-to-noise-ratio.
2.3 Surface Functionalization and Reaction Recognition When a sensor is needed, e.g., to identify whether a specific molecule is present in a solution or not, one wants to be sure that only the molecule under consideration is checked for and no similar molecules are involved in the same measurement. In other words a sensor needs to be specific. How is it possible to ensure that the buildup of the above discussed adlayers is specific for only one molecular species? This is typically done by functionalizing the surface with a molecule which allows the molecule under consideration to bind specifically, via a recognition reaction or a guest–host reaction to it [39–42]. All other molecules should not bind to the immobilized matrix, avoiding unspecific binding. Figure 2.8 shows a schematic drawing of a waveguide carrying two different immobilized binding sites (oval and angular) to specifically bind only one fitting molecule each. Typically a waveguide carries only one species of binding site.
28
Silvia Mittler and Bernhard Menges
binding agent
host matrix
waveguide substrate
F i g u r e 2.8. Schematic representation of specific binding on a waveguide: a waveguide on a substrate with two different immobilized binding sites (oval and angular) being able to specifically recognize and bind one species only. Typically one waveguide carries one functionalization only to avoid crosstalk. The scheme is vertically not to scale. The waveguide dimensions are between 200 nm and 1 m, whereas the first immobilized layer has a thickness on the order of a few angstroms to a few nanometers.
Various chemical strategies are present to immobilize recognition sites on surfaces from Langmuir-Blodgett films to self-assembled monolayers [43–48]. A covalent link to the substrate enhances the stability of the functionalization on the surface, when liquids are rinsed across it. It depends on the kind of materials which are supposed to be connected. Glasses having -OH groups present at the surface after cleaning can be functionalized by a process called silanization. Here a covalent bond is formed between the oxygen of the surface with a Si from the immobilized silane [R(with function)- Si-R3 ] undergoing several intermediate reaction states [39, 40]. Metal surfaces are easily functionalized via self-assembled monolayers (SAMs) formed out of molecules having a thiol, a sulfide, or a disulfide function in a spacer group [39, 43–47]. Sometimes multistep functionalizations are necessary: e.g., first a silanization which allows use of the immobilized silane function R to continue immobilizing the desired biological or chemical function [40, 48]. Multistep functionalization strategies cover established biological guest–host systems such as the biotin– avidin system [49–52] (Figure 2.9), but also approaches of metal nanoparticles [53, 54] have been made. But whatever the choice of the chemistry adequate to link the “catcher” molecule to a surface, one has to make sure that the active binding site is accessible and that no steric hindrance occurs during the binding caused by the geometry of the catcher, the recognized molecule and the bound system. Various authors have shown that steric hindrance can be easily overcome by mixing the active catcher molecule with an inactive dilutor molecule (Figure 2.9). In most cases, when no phase separation in this binary mixture occurs [55–57], this decouples the binding sites laterally from each other and then provides easy
2. Evanescent Waves as Nanoprobes
29
a
change in coupling angle TM0-mode [°]
5.24 5.23
biotinylated oligonucleotide
streptavidin
complementary oligo nucleotide
5.22 5.21 5.20 5.19
na= 1.381 da= 12.7 nm
na= 1.388 da= 11 nm na = 1.4 da= 8nm
5.18 5.17
waveguide substrate
5.16 0
10
20
30
40
50
60
70
80
time [minutes]
b -Biotin-(T)30 ACG TCA GTC TCA CCC-3’ 3’-TGC AGT CAG AGT GGG TGT TAT AAG TGA GTC GGT GAT GAT GGA GAC ATT GA-5’
F i g u r e 2.9. (a) Response of the coupling angle with time for a three-step surface functionalization scheme and an oligonucleotide hybridization reaction. The inset describes the layer system: a biotinylated thiol layer is immobilized on the waveguide, followed by streptavidin, a biotinylated oligonucleotide as catcher, and the complementary oligonucleotide for hybridization of the molecule under consideration to be detected. The given data are the overall layer thicknesses and refractive indices of the multilayer systems. (b) The oligonucleotide sequences.
accessibility [58–61]. If a recognition reaction involves a large interdigitation of the two molecules (e.g., for DNA hybridization) or binding into a pocket (e.g., biotin binds into a binding pocket in avidin), the molecules have to be located on a flexible spacer to overcome steric hindrance along the binding direction. The inset of Figure 2.9a explains most of the above-mentioned characteristics for efficient multistep functionalization. On top of the waveguide a mixture of biotinylated silanes with a long alkyl chain mixed with inactive OH-terminated short-chain alkyl silanes is immobilized. Then a layer of streptavidin is bound to the biotin functionalization [62, 63]. In the next step, a biotinylated oligonucleotide [64–67] is bound to the steptavidin, exposing binding sites for biotin at its new surface. In this case, the synthetic oligonucleotide consists of 30 T (thymine) units as a spacer and 5 codons as the catcher [64–67]. The recognized molecule consists of the 5 matching codons and 12 additional random condons
30
Silvia Mittler and Bernhard Menges
to enhance the optical signal by additional binding material with a refractive index different from the solvent. The oligonucleotides are depicted in Figure 2.9b. The overall sensitivity of an integrated optical device does not only depend on the physical sensitivity S as defined above. It also depends on the chemical sensitivity of the binding, recognizing pair: the affinity constant. Since a recognition reaction, e.g., from a guest G into or to a host H, is reversible, equilibrium is established, which can be described as: H + G ↔ HG. According to the law of mass action, this can be written as K=
HG HG
with [HG] the equilibrium concentration of the bound system, [H] and [G] the concentrations of the host and the guest, respectively, and K the equilibrium or affinity constant. In the case where half of the available guests are occupied, HG = H and then K = 1/G. So the higher the numerical value of K, the larger is the affinity, and the less “free” guests are found. Therefore, the affinity constant has a direct impact on the overall sensitivity of a device, because it controls the time average of the number of occupied binding sites. This number is directly correlated with the time average of the presence of the adlayer. Only when the adlayer is as complete as possible can the full physical sensitivity be achieved. The operation of a sensor does not necessarily mean only the detection of molecules binding to a recognition site. It can also mean a detection of changes within the adlayer which lead to alterations of the thickness and/or the refractive index. These changes can have various causes including photochemical reactions, swelling, temperature effects such as transitions, aging, and wear. The evanescent field can also be used to illuminate ultrathin samples located on top of a waveguide with the two specific polarization directions. This leads to two main applications: evanescent absorption spectroscopy [69–73] and evanescent microscopy [74–79]. A huge number of integrated optical sensors use the evanescent field to excite fluorescence labels attached to the molecules under consideration when they bind to their recognition site [80, 81, 82]. This chapter does not cover these very sensitive (bio) chemical sensors; rather, it covers only label-free methods. It also does not include all the studies in which surface plasmon resonances of gold dielectric interfaces on a waveguide are coupled to waveguide modes [83–85].
2.4 Examples 2.4.1 Monitoring of a Photochemical Isomerization Reaction in a Waveguide 1.1 m Thick Mesoionic 6-oxo-1,6-dihydropyrimidin-3-ium-4-oleate (Figure 2.10a) was incorporated as a part of a side chain into a polymer. The mesoion is connected to the
2. Evanescent Waves as Nanoprobes
31
a R1 R4
+
N
N
R1
R2
h*v
R2
R4
N
N
O-
O
R3
O
R3
O
b change in coupling angle [°]
0.00 TE0-mode TE1-mode TE2-mode
–0.05 –0.10 –0.15 –0.20 –0.25 –0.30 –0.35
0
2
4
6
8
10
12
14
16
18
20
time of irradiation [h]
c 22 0.000
20 16 14
–0.002
12 10
–0.003
8 6
–0.004
4
change in thickness [nm]
change in refractive index
18 thickness
–0.001
2
–0.005
refractive index
0
–0.006 0
2
4
6
8
10
12
14
16
18
–2 20
time of irradiation [h]
F i g u r e 2.10. (a) Photoreaction of mesoionic 6-oxo-1,6-dihydropyrimidin-3-ium-4oleate. (b) The change of three TE modes with illumination time. (c) Thickness and refractive index change with illumination time calculated from (b).
32
Silvia Mittler and Bernhard Menges
polymer main chain via a spacer group R1 . The rests R2 and R4 are benzene rings and R3 is a CH3 group. Further chemical details and synthesis strategies have been given elsewhere [86]. The mesoion changes its planar mesoionic structure into an angled bis(-lactam) structure on irradiation in the near-UV. This leads to a decrease in polarizability and to a higher steric demand. The polymer was spin-coated as a waveguide onto a fused silica substrate carrying a previously fabricated coupling grating [87] with a periodicity = 797 nm. A HeNe laser at a wavelength of 632.8 nm was used to couple into waveguide modes at both polarization directions. In order to photoisomerize the polymer, a linearly polarized beam from a HeCd laser (442 nm) was incident at 0 to the coupling spot of the waveguide modes. Three modes of each polarization were found and followed with illumination time. Figure 2.10a shows the change in coupling angles versus illumination time for the TE modes. For all data sets the refractive index and thickness values were calculated (Figure 2.10c). Both polarization directions gave identical results; thus, a homogeneous refractive index and refractive index decrease were found. The diminished polarizability of the mesoion and the swelling of the film due to the higher steric demand after photobleaching are responsible for the refractive index drop. The increase in film thickness is direct evidence for the photoreaction and the enhancement of the necessary space for the photo-switched mesoion. This example shows how a thick film in the micrometer regime, and changes in it, can be analyzed using waveguide spectroscopy on a known substrate.
2.4.2 Label-Free Detection of Oligonucleotide Hybridization As discussed in Section 2.3, Figure 2.9 shows a multilayer functionalization on a waveguide using the biotin–streptavidin system. The figure exhibits changes in the TE mode coupling angles of a commercial Ta2 O5 waveguide (Unaxis) with a thickness of 160 nm and a coupling grating of = 360 nm. The coupling angle changes on rinsing a new solution along the waveguide and binding the next species onto it. The first step is streptavidin adsorption, the second step the binding of the catcher oligonucleotide, and the third step the hybridization reaction of the oligonucleotides. From both the TE and the TM mode measurements the refractive index and the thickness of the entire adlayers on the waveguide were calculated for all steps. Streptavidin on the biotin–silane layer yields a refractive index of 1.4 and an overall thickness of 8 nm. This is a typical data set found for a water-swollen silane–protein system [88]. Immobilizing the catcher oligonucteotide leads to an increase in thickness by 3 nm to 11 nm and a decrease in refractive index to 1.388. This decrease in refractive index is due to a non-densely packed film: water is located in-between the oligonucleotide molecules. The final hybridization reaction leads to a further decrease in refractive index to 1.381, and an increase in thickness to 12.7 nm. Again the refractive index drop shows the water involved in the films deposited.
2. Evanescent Waves as Nanoprobes
33
Taking DNA data into account [64, 65], a densely packed 45-mer would lead to an estimated film thickness increase of 15.3 nm. Obviously this is not seen by waveguide spectroscopy. The films are not densely packed and probably not even ordered, showing only elongated chains sticking out perpendicularly as drawn in Figure 2.9a. The same is true for the hybridization reaction with an additional 35-mer. The interpretation of such data has to be done with great care. Only one TE and one TM mode can be measured at that high sensitivity (see Figure 2.6). The data evaluation for thickness and refractive index is then done under the assumption of an isotropic film. The film here is not completely isotropic because of its layer structure. Therefore, only the overall data are calculated and neither single layer data nor any concentration data are given. The data are estimations, only showing trends. Additional information is necessary, such as the use of two more waveguide modes by choosing a thicker waveguide and losing sensitivity (Figure 2.6), or by a calibration measurement. This example shows how a high-sensitivity waveguide can detect the binding of even minute amounts of molecules in a yes–no answer fashion: if a shift in the coupling angle is measured, the molecule under consideration is present (if the recognition reaction is specific). If no shift is seen, no binding occurred; the molecule was not present or only present in a concentration below the detection limit. Any other information, e.g. mismatches in the oligonucleotide hybridizing, has to be found by additional investigations [89–93].
2.4.3 Swelling of Thin Polymer Films in Solvent An ultrathin film of polyallylamine with a thickness of 7.7 nm was deposited by a plasma polymerization reaction onto a commercial Ta2 O5 waveguide (Unaxis) with a thickness of 160 nm and a coupling grating of = 360 nm. The details of the film formation are published elsewhere [94–96]. The film was then placed at room temperature into ethanol. Ethanol is a good solvent for polyallylamine and should be able to intrude into the film and swell it. The coupling angles for both polarization directions were measured with increasing time in ethanol. Then the sample was dried in an oven. After cooling back to room temperature, the coupling angles were followed in time in regular air. Figure 2.11 shows the thickness (a) and the refractive index (b) data calculated from the optical waveguide data. The film was found to be isotropic. The film thickness increases over hours when located in ethanol. Even after 18 hours no equilibrium plateau was reached, but an increase in film thickness from 7.7 nm to 11 nm. The thorough drying of the film leads to an even smaller film thickness in comparison to the newly prepared film. This means that during the drying process a small amount of molecular material must have been removed, which was present in the newly prepared films. These are probably solvent leftovers from the cleaning procedure. A small increase in film thickness is detected in air. Obviously the film takes up gases from the air. The refractive index, on the other hand, decreases with ethanol uptake. This is due to a dilution process. As can be seen from Figure 2.11b, the refractive
34
Silvia Mittler and Bernhard Menges
a
11.5 11.0
ethanol
thickness [nm]
10.5
drying the film under vacuum
10.0 9.5 9.0 8.5
air
8.0 7.5 7.0
0
5
10
15
20
25
30
35
40
35
40
time [h]
b
1.64
refractive index
1.63 air
1.62 1.61 1.60 1.59
drying the film under vacuum
1.58 1.57
ethanol
1.56 0
5
10
15
20
25
30
time [h]
F i g u r e 2.11. (a) Thickness and (b) refractive index behavior of a plasma-deposited polyallylamine film on swelling in ethanol, drying, and placement in air.
index of the dried, mostly pure material is 1.636. The intake of ethanol having a refractive index of 1.361 dilutes the high refractive index of the polymer and lets it decrease with an increasing amount of the low-index solvent. It can be recovered by drying the film and slowly decreases again during uptake of air gases. This example shows how a waveguide can be used to monitor swelling effects due to chemical uptake in thin films within the nanometer regime.
2.4.4 Glass Transition Measurements in Polymer Mono- and Multi-layer LB Films The glass transition Tg (freezing of segmental movement) in thin polymer films has attracted the interest of polymer researchers for quite some time, because it has been unclear whether a thin film material would behave differently from
2. Evanescent Waves as Nanoprobes
35
the bulk [97–111]. Waveguide attempts were very successful, here using “thick” waveguides and measuring the glass transition in the waveguide material itself [105–107]. The glass transition typically appears as a kink in the temperature– waveguide mode position, because at the glass transition the thermal expansion d coefficient = d1 T (with d the thickness and T the temperature) changes as n [106]. It was found that well as the thermal refractive index coefficient k = T indeed the glass transition decreases with decreasing film thickness, as long as no interaction between the substrate and the polymer is present. Free standing films were also investigated with ellipsometry [90]. The smallest thickness films were prepared by LB technology [43–48] and investigated by surface plasmon resonance spectroscopy, an evanescent technology similar to waveguide spectroscopy, but with less information gain [106, 112]. Figure 2.12a shows the coupling angle behavior of the TE0 mode of a commercial Ta2 O5 waveguide (Unaxis) with a thickness of 160 nm and a coupling grating of = 360 nm for = 6328 nm with temperature changing (both increasing and decreasing). The coupling angle position increases with
a 13.42
coupling angle TE0-Mode [°]
13.40
heating cooling
13.38
linear regression
13.36 13.34 13.32 13.30 13.28 13.26 13.24 20
40
60
80
100
120
140
160
temperature [°C]
F i g u r e 2.12. (a) Coupling angle behavior of the TE0 mode of a Ta2 O5 waveguide with temperature change: red data represent the heating, blue data the cooling. (b) The structure formula of the polyamide acid and the reaction into the polyamide releasing water. Two derivatives with different spacer lengths n = 4 and n = 6 were investigated. (c) Position of the coupling angle of the TM0 mode of the Ta2 O5 waveguide with one monolayer of the n = 6 spacer polymer in the polyamide form after heating with decreasing temperature. The lines are linear regressions to the upper (blue) or lower (red) data points, respectively. The temperature where both regressions intersect is the glass transition temperature of that monolayer.
HOOC
HNCO
R=
N
CH3 C CH3
C6H13
N
O
(CH2)n
N
O
CH3 C CH3
O
polyamide acid
O
O
F i g u r e 2.12. (Continued)
[ CONH R
COOH n
[
b
heat
–2n H2O
[ O
N
O
R=
O
N
CH3 C CH3
C6H13
N
O
(CH2)n
N
polyimide
O
O
CH3 C CH3
O
O
N
O R
n
[
2. Evanescent Waves as Nanoprobes
c
37
1.060 1.055
coupling angle TM0-mode [°]
1.050 1.045 1.040 1.035 1.030 1.025 1.020 1.015 1.010 1.005 1.000 25 30 35 40 45 50 55 60 65 70 75 80 85 90 95 100 105 110 temperature [°C]
F i g u r e 2.12. (Continued)
increasing temperature due to the thermal expansion and the temperature refractive index coefficient of the waveguide sample itself. No hysteresis is observed. The data showed an identical behavior for the TM mode. This proved that the Ta2 O5 waveguide is an excellent substrate for materials which show temperature-driven transitions. Using the LB technique, monolayers and multilayers of polyamide acid can be transferred in the condensed state to Ta2 O5 waveguides and subsequently heated to form polyimide under water production (Figure 2.12b). The bulk glass transition temperatures Tg for the two derivatives were determined via DSC investigations [113]. The polyimide with a spacer group length of n = 4 shows a Tg of ∼ 88 C and the n = 6 spacer polymer a Tg of ∼ 58 C. A single monolayer of the n = 6 material was transferred to the waveguide and converted to the polyamide, then investigated with respect to the TM waveguide mode position with decreasing temperature. Figure 2.12c shows the waveguide mode coupling data together with linear regressions to the upper (red line) and lower (blue line) temperature data. Clearly two different slopes are found. The intersection of the two lines, the kink, indicates a glass transition temperature Tg at ∼ 62 C very close to the bulk value at ∼ 58 C. Because the glass transition is not a very sharp transition, these two values are identical within experimental error. Contrary to most of the literature, no decrease in the glass transition due to the ultrathin film geometry was found, probably because interactions between the substrate and the polymer film were not inhibited. Because the waveguide setup allows for anisotropy investigations, multilayer samples were investigated with the two polarization directions. Figure 2.13a shows a nine-layer sample of the n = 6 spacer material investigated with the TM mode, whereas Figure 2.13b
38
Silvia Mittler and Bernhard Menges
a 3.16
coupling angle TM0-mode [°]
3.15 3.14 3.13 3.12 3.11 3.10 3.09 3.08 20
30
40
50
60
70
80
90
100
110
120
temperature [°C]
b 13.94 13.93 coupling angle TE0-mode [°]
13.92 13.91 13.90 13.89 13.88 13.87 13.86 13.85 13.84 20
30
40
50
60
70
80
90
100
110
120
temperature [°C]
F i g u r e 2.13. (a) Coupling angle behavior of the TM0 mode for a nine layer sample of the n = 6 spacer material and (b) coupling angle behavior for a nine layer sample of the n = 4 spacer material.
shows data for a nine layer sample of the n = 4 material with the TE mode. Not surprisingly, the TM mode is able to show the same glass transition temperature for the thicker sample, but surprisingly the TE mode does not detect any kink with two different slopes in the temperature data, but an offset at around 70 C,
2. Evanescent Waves as Nanoprobes
39
which is a little below the Tg value of the n = 4 bulk material (∼ 88 C). The physicochemical reason for this behavior is not yet well understood and it is still under investigation. The cause of this anisotropic behavior lies probably within the anisotropic structure of the monolayers fabricated by LB technology. The hydrophilic main chain of the polymer is “separated” by hydrophobic interactions from the hydrophobic side chains on the air–water interface, leading to a transferred first monolayer which is attached with the main chain to the hydrophilic substrate with side chains randomly sticking out. This looks like a nanoscopic comb. The TM mode then preferentially probes the side chains carrying the spacers, which are partly responsible for the precise position of Tg . The TE mode preferentially probes the main chain, which seems to only indirectly couple to Tg , showing an offset instead of a kink involving changes in physical constants. This example exhibits how waveguide spectroscopy can be used for materials research down to monolayer sensitivity including anisotropic effects which are not seen with any other method at these sample thicknesses.
2.4.5 Evanescent Scattering Microscopy As mentioned above, the evanescent field of a waveguide can also be used to excite molecules, typically in technologies involving fluorescence labels. On the other hand, one finds, looking at the mechanisms leading to waveguide losses, that with waveguides having surfaces that have not been prepared smoothly, light escapes — it is scattered by surface inhomogeneities. This effect is used in evanescent scattering microscopy [74, 75]. Here a laterally structured thin film sample is placed on a waveguide into the evanescent field of the propagating modes and the scattered light is observed with a standard microscope perpendicular under 0 angle distortion free. Figure 2.14 shows a typical setup. A polarized laser beam is coupled by a grating coupler to a specific mode (polarization and mode number). A cuvette enables microscopy to be performed in either a solvent or an aqueous environment. Figure 2.15 shows images (a) with the TE3 mode and (b) with the TM3 mode, taken from a four-mode
polarizer
mirror on rotagen stage
camera
laser
microscope objective
lenses
cuvette grating
waveguide with sample
F i g u r e 2.14. Experimental setup for evanescent waveguide scattering microscopy.
40
Silvia Mittler and Bernhard Menges
a
b
F i g u r e 2.15. Scattering microscopy image taken of a 40-nm-thick laterally patterned photoresist sample on illuminating with (a) the TE3 mode and (b) the TM3 mode.
ion exchanged waveguide in BK7 glass with a 40-nm-thick laterally patterned photoresist sample. The photoresist appears bright in the images, because it creates inhomogeneities in the evanescent field which lead to scattered photons giving a bright impression. The dark areas are the pure waveguide surfaces which do not scatter and are therefore dark. The TE mode shows a higher contrast than the TM mode. It was also found that with increasing mode number, for both polarization directions the contrast increased. Simulations of the evanescent field strength have demonstrated that the contrast is directly correlated with the present strength of the evanescent field occupied by the scattering film. In addition, the contrast is a function of the refractive index contrast between the scattering material and the surrounding material. A photoresist–air image shows much higher contrast than a photoresist–water image. Because a conventional microscope is used, the lateral resolution is limited by diffraction and is therefore in the micrometer regime. The resolution in the z-direction is at least 40 nm, as measured. The minimal thickness still being seen with decent contrast has not yet been determined.
2.5 Conclusion As we have seen in this selection of examples, waveguide spectroscopy and especially the evanescent field accompanied by this technology offer a wide spectrum of analytical possibilities. Because the system is coupled to at least two physical parameters of the waveguide itself or an adlayer — thickness and refractive index — this technology can be applied to nearly any thin film analysis problem, where at least one of these physical parameters is modified. Because the waveguides can be fabricated out of robust inorganic materials, the measurement environment can be harsh: from high temperatures to chemical environments. Samples such as nanoparticles which cannot be described by the word “film,” meaning that there is no lateral dimension which is “infinite” in parallel direction
2. Evanescent Waves as Nanoprobes
41
to the waveguide surface, cannot be analyzed by this technology so far, because the theoretical background for data analysis is based in the Fresnel equations — which in their classical form are valid only for layer systems with homogeneous thicknesses over large dimensions. Nevertheless, by additionally taking into account other light-guiding systems such as surface plasmon spectroscopy, and waveguide architectures and applications (from waveguides with metal coatings, surface plasmon waveguide mode coupling, through to devices based on fluorescence to waveguide absorption spectroscopy and microscopy technologies), we see an amazing spectrum of nanoscale analytical possibilities. Further research and development, combining nanostructures such as metal nanoparticles or photonic crystals with conventional waveguide geometries and architectures, will lead to new physical effects and definitely to new nano-optical devices for applications from data storage to all-optical switching, communications technology, and, again, the analysis of nanostructures. Acknowledgments. The authors thank all co-workers and colleagues who have contributed over the years in using waveguides and their fields as analytical tools.
References 1. Bergmann-Schaefer, Lehrbuch der Experimentalphysik, Band III Optik, de Gruyter, Berlin (1978). 2. C. Gerthsen, H.O. Kneser, and H. Vogel, Physik, 13th edition, Springer-Verlag, Berlin (1977). 3. J.D. Jackson, Classical Electrodynamics, 3rd edition, Wiley, New York (1999). 4. M.J. Adams, An Introduction to Optical Waveguides, Wiley, New York (1981). 5. R.G. Hunsperger, Integrated Optics: Theory and Technology, 4th edition, SpringerVerlag, Berlin (1995). 6. T. Tamir (Ed.), Integrated Optics, 2nd edition, Springer-Verlag, Berlin (1979). 7. A.W. Snyder and J.D. Love, Optical Waveguide Theory, Chapman & Hall, London (1983). 8. R. Syms and J. Cozens, Optical Guided Waves and Devices, McGraw–Hill, New York (1992). 9. D. Marcuse, Theory of Dielectric Optical Waveguides, 2nd edition, Academic Press, Boston (1991). 10. G.P. Agrawal, Applications of Nonlinear Fiber Optics, Academic Press, San Diego (2001). 11. C.D. Chaffee, Building the Global Fiber Optics Superhighway, Kluwer Academic/ Plenum, New York (2001). 12. G.D. Cole, Computer Networking for Systems Programmers, Wiley, New York (1990). 13. R. Ulrich and R. Torge, Measurement of thin film parameters with a prism coupler, Appl. Opt. 12, 2901–2908 (1973). 14. W. Karthe and R. Müller, Integrierte Optik, Akademische Verlagsgesellschaft Geest & Portig, Leipzig (1991).
42
Silvia Mittler and Bernhard Menges
15. T. Liu and R.J. Samuels, Physically corrected theoretical prism waveguide coupler model, J. Opt. Soc. Am. A 21, 1322–1333 (2004). 16. M.A. Uddin, H.P. Chan, and C.K. Chow, Thermal and chemical stability of a spincoated epoxy adhesive for the fabrication of a polymer optical waveguide, Chem. Mater. 16, 4806–4811 (2004). 17. X. Zhang, H.J. Lu, A.M. Soutar, and X.T. Zeng, Thick UV-patternable hybrid sol-gel films prepared by spin coating, J. Mater. Chem. 14, 357–361 (2004). 18. D.A. Chang-Yen and B.K. Gale, An integrated optical oxygen sensor fabricated using rapid-prototyping techniques, Lab on a Chip 3, 297–301 (2003). 19. G.M. Wang, H. Ai, X. Liu, and F.G. Tao, A nonlinear optical waveguide made up of alternating NMOB/CdA multilayers, J. Opt. A Pure Appl. Opt. 4, 587–590 (2002). 20. M. Yanagida, A. Takahara, and T. Kajiyama, Construction of defect-diminished fatty acid Langmuir-Blodgett film and its optical waveguide properties, Bull. Chem. Soc. Jpn. 72, 2795–2802 (1999). 21. W. Hickel, G. Appel, D. Lupo, W. Prass, and U. Scheunemann, Langmuir-Blodgett multilayers from polymers for low-loss planar waveguides, Thin Solid Films 210, 182–184 (1992). 22. C. Bosshard, M. Florsheimer, M. Kupfer, and P. Günter, Cerenkov-type phasematched 2nd- harmonic generation in DCANP Langmuir-Blodgett-film waveguides, Opt. Commun. 85, 247–253 (1991). 23. S. Mittler-Neher, A. Otomo, G.I. Stegeman, C. Y.-C. Lee, R. Mehta, A.K. Agrawal, and S.A. Jenekhe, Waveguiding in substrate and freestanding films of insoluble polymers, Appl. Phys. Lett. 62, 115–117 (1993). 24. G. Ihlein, B. Menges, S. Mittler-Neher, J.A. Osaheni, and S.A. Jenekhe, Channel waveguides of insoluble conjugated polymers, Opt. Mater. 4, 685–689 (1995). 25. C.C. Huang, D.W. Hewak, and J.V. Badding, Deposition and characterization of germanium sulphide glass planar waveguides, Opt. Express 12, 2501–2506 (2004). 26. N.J. Goddard, K. Singh, J.P. Hulme, C. Malins, and R.J. Holmes, Internallyreferenced resonant mirror devices for dispersion compensation in chemical sensing and biosensing applications, Sens. Actuat. A 100, 1–9 (2002). 27. D.P. Bour, M. Kneissl, C.G. Van de Walle, G.A. Evans, L.T. Romano, J. Northrup, M. Teepe, R. Wood, T. Schmidt, S. Schoffberger, and N.M. Johnson, Design and performance of asymmetric waveguide nitride laser diodes, IEEE J. Quantum Electron. 36, 184–191 (2000). 28. Q. Gao, M. Buda, H.H. Tan, and C. Jagadish, Room-temperature preperation of InGaAsN quantum dot lasers grown by MOCVD, Electrochem. Solid State Lett. 8, G57–G59 (2005). 29. M. Born and E. Wolf, Principles of Optics, Pergamon Press, London (1970). 30. S.I. Najafi, Introduction to Glass Integrated Optics, Artech House, Boston (1992). 31. R.V. Ramaswamy and R. Srivastavam, Ion-exchanged glass waveguides — a review, J. Lightwave Technol. 6, 984–1002 (1988). 32. P.D. Townsend, P.J. Chandler, and L. Zhang, Optical Effects of Ion Implantation, Cambridge University Press, Cambridge (1994). 33. S. Mittler-Neher and H. Einsiedel, Photothermal beam deflection techniques: a useful tool for integrated optics, Proc. SPIE 2852, 248–257 (1996). 34. S. Mittler-Neher, Linear optical characterization of nonlinear optical polymers for integrated optics, Macromol. Chem. Phys. 199, 513–523 (1998).
2. Evanescent Waves as Nanoprobes
43
35. H. Einsiedel, M. Kreiter, M. Leclerc, and S. Mittler-Neher, Photothermal beam deflection spectroscopy in the near IR on poly[3-alkylthiophene]s, Opt. Mater. 10, 61–68 (1998). 36. G. Lenz and J. Salzman, Eigenmodes of multiwaveguide structures, J. Lightwave Technol. 8, 1803–1809 (1990). 37. W. Lukos and K. Tiefenthaler, Sensitivity of integrated optical grating and prism couplers as (bio)chemical sensors, Sensors Actuat. 15, 273–284 (1988). 38. K. Tiefenthaler and W. Lukosz, Sensitivity of grating couplers as integrated-optical chemical sensors, J. Opt. Soc. Am. B 6, 209–220 (1989). 39. P. Mohr, M. Holtzhauer, and G. Kaiser, Immunosorption Techniques: Fundamentals and Applications, Akademie-Verlag, Berlin (1992). 40. T. Cass and F.S. Ligler (Eds.), Immobilized Biomolecules in Analysis, Oxford University Press, Oxford (1998). 41. E.M. Blalock (Ed.), A Beginner’s Guide to Microarrays, Kluwer Academic, Boston (2003). 42. D. Wild (Ed.), The Immunoassay Handbook, 2nd edition, Nature Publishing Group, New York (2001). 43. A. Ulman, An Introduction to Ultrathin Organic Films: From Langmuir-Blodgett to Self-Assembly, Academic Press, Boston (1991). 44. A. Ulman, Formation and structure of self-assembled monolayers, Chem. Rev. 96, 1533–1554 (1996). 45. A. Ulman, Organic Thin Films and Surfaces: Directions for the Nineties, Academic Press, San Diego (1995). 46. A. Ulman (Ed.), Characterization of Organic Thin Films, Butterworth-Heinemann, Boston (1995). 47. F. Schreiber, Structure and growth of self-assembling monolayers, Prog. Surf. Sci. 65, 151–256 (2000). 48. M.C. Petty, Langmuir-Blodgett Films: An Introduction, Cambridge University Press; Cambridge (1996). 49. M. Wilchek and E.A. Bayer, Avidin-Biotin Technology, Academic Press, San Diego (1990). 50. V.C. Yang and T. T. Ngo (Eds.), Biosensors and Their Applications, Kluwer Academic/Plenum, New York (2000). 51. D.Möbius and R. Miller (Eds.), Organized Monolayers and Assemblies: Structure, Processes, and Function, Elsevier, Boston (2002). 52. C.M. Niemeyer, Bioconjugation Protocols: Strategies and Methods, Humana Press, Totowa, NJ (2004). 53. S. Busse, J. Käshammer, S. Krämer, and S. Mittler-Neher, Gold and thiol surface functionalized integrated optical Mach-Zehnder interferometer for sensing purposes, Sens. Actuat. B 60, 148–154 (1999). 54. Z.-M. Qi, N. Matsuda, T. Yoshida, A. Takatsu, and K. Kato, Colloidal gold submonolayer- coated thin-film glass plates for waveguide-coupled surface plasmon resonance sensors, Appl. Opt. 42, 4522–4528 (2003). 55. N.J. Brewer and G.L. Leggett, Chemical force microscopy of mixed self-assembled monolayers of alkanethiols on gold: Evidence for phase separation, Langmiur 20, 4109–4115 (2004). 56. F.Q. Fan, C. Maldarelli, and A. Couzis, Fabrication of surfaces with nanoislands of chemical functionality by the phase separation of self-assembling monolayers on silicon, Langmuir 19, 3254–3265 (2003).
44
Silvia Mittler and Bernhard Menges
57. K. Aoki, Theory of phase separation of binary self-assembled films, J. Electroanal. Chem. 513, 1–7 (2001). 58. J. Spinke, M. Liley, F.-J. Schmitt, H.-J. Guder, L. Angermaier, and W. Knoll, Molecular recognition at self-assembled monolayers: Optimization of surface functionalization, J. Chem. Phys. 99, 7012–7019 (1993). 59. J. Spinke, M. Liley, H.-J. Guder, L. Angermaier, and W. Knoll, Molecular recognition at self-assembled monolayers: the construction of multicomponent multilayers, Langmuir 9, 1821–1825 (1993). 60. M. Weisser, G. Nelles, G. Wenz, and S. Mittler-Neher, Guest–host interaction with immobilized cyclodextrins, Sens. Actuat. B 38–39, 58–67 (1997). 61. M. Weisser, J. Käshammer, J. Matsumoto, F. Nakamura, K. Ijiro, M. Shimomura, and S. Mittler-Neher, Adenin–uridin base pairing at the water-solid-interface, J. Am. Chem. Soc. 122, 87–95 (2000). 62. G. Tovar, L. Angermaier, P. Sluka, H.G. Batz, and W. Knoll, Molecular recognition at biotin-functionalized oxidic surfaces: Biofunctional self-assembly of proteins, Abstr. Pap. Am. Chem. Soc. 212, 12 (1996) Part 1. 63. M. Weisser, G. Tovar, S. Mittler-Neher, W. Knoll, F. Brosinger, H. Freimuth, M. Lacher, and W. Ehrfeld, Specific bio-recognition reactions observed with an integrated Mach-Zehnder interferometer, Biosens. Bioelectron. 14, 405–411 (1999). 64. A.L. Lehninger, Principles of Biochemistry, Worth Publishers, New York (1982). 65. D.A. Metzler, Biochemistry: The Chemical Reactions of Living Cells, Volume 1, 2nd edition, Harcourt Academic Press, San Diego (2001). 66. G. Stengel, F. Höök, and W. Knoll, Viscoelastic modeling of template-directed DNA synthesis, Anal. Chem. 77 (11)3709–3714(2005). 67. G. Stengel and W. Knoll, Surface plasmon field-enhanced fluorescence spectroscopy studies of primer extension of surface-bound oligonucleotides, Nucleic Acids Res. 33 (7)E69 (2005). 68. V. Ruddy, Nonlinearity of absorbency with sample concentration and path-length in evanescent wave spectroscopy using optical fiber sensors, Opt. Eng. 33, 3891–3894 (1994). 69. K. Kato, A. Takatsu, N. Matsuda, R. Azumi, and M. Matsumoto, A slab waveguide absorption spectroscopy of Langmuir-Blodgett films with a white light excitation source, Chem. Lett. 6, 437–438 (1995). 70. H. Kawai, K. Nakano, and T. Nagamura, White light optical waveguide detection of transient absorption spectra in ultrathin organic films upon pulsed laser excitation, Chem. Lett. 12, 1300–1301 (2001). 71. J.H. Santos, N. Matsuda, Z.M. Qi, A. Takatsu, and K. Kato, Effect of surface hydrophilicity and solution chemistry on the adsorption behaviour of cytochrome c in quartz studied using slab optical waveguide spectroscopy, IEEE Trans. Electron. E85-C, 1275–1281 (2002). 72. J.T. Bradshaw, S.B. Mendes and S.S. Saavedra, A simplified broadband coupling approach applied to chemically robust sold-gel, planar integrated optical waveguides, Anal. Chem. 74, 1751–1759 (2002). 73. F.T. Bradshaw, S.B. Mendes, N. Armstrong, and S.S. Saavedra, Broadband coupling into a single-mode, electroactive integrated optical waveguide for spectroelectrochemical analysis of surface-confined redox couples, Anal. Chem. 75, 1080–1088 (2003). 74. F. Thoma, U. Langbein, and S. Mittler-Neher, Waveguide scattering microscopy, Opt. Commun. 134, 16–20 (1997).
2. Evanescent Waves as Nanoprobes
45
75. F. Thoma, J. Armitage, H. Trembley, B. Menges, U. Langbein, and S. Mittler-Neher, Waveguide scattering microscopy in air and water, Proc. SPIE 3414, 242–249 (1998). 76. W. Knoll, W. Hickel, M. Sawodny, and J. Stumpe, Polymer interface and ultrathin films characterization by optical evanescent wave techniques, Makromol. Chem. Makromol. Symp. 48, 363–379 (1991). 77. W. Knoll, W. Hickel, M. Sawodny, J. Stumpe, and H. Knobloch, Novel optical techniques for the analysis of polymer surfaces and thin films, Fresenius J. Anal. Chem. 341, 272–278 (1991). 78. E.F. Aust and W. Knoll, Electrooptical waveguide microscopy, J. Appl. Phys. 73, 2705–2708 (1993). 79. M. Bastmeyer, H.B. Deising, and C. Bechinger, Force exertion in fungal infection, Annu. Rev. Biophys. Biomol. Struct. 31, 321–341 (2002). 80. X.F. Wang and U.J. Krull, Synthesis and fluorescence studies of thiazole orange tethered onto oligonucleotide: Development of a self-contained DNA biosensor on a fiber optic surface, Bioorg. Med. Chem. Lett. 15, 1725–1729 (2005). 81. R.A. Yotter, L.A. Lee, and D.M. Wilson, Sensor technologies for monitoring metabolic activity in single cells — Part I: Optical methods, IEEE Sens. J. 4, 395–411 (2004). 82. T.J. Pfefer, L.S. Matchette, A.M. Ross, and M.N. Ediger, Selective detection of fluorophore layers in turbid media: The role of fiber-optic probe design, Opt. Lett. 28, 120–122 (2003). 83. M. Weisser, B. Menges, and S. Mittler-Neher, Multimode integrated optical sensor based on absorption due to resonantly coupled surface plasmons, Proc. SPIE 3414, 250–256 (1998). 84. M. Weisser, B. Menges, and S. Mittler-Neher, Refractive index and thickness determination of monolayers by multi mode waveguide coupled surface plasmons, Sens. Actuat. B 56, 189–197 (1999). 85. M. Weisser, J. Käshammer, J. Matsumoto, F. Nakamura, K. Ijiro, M. Shimomura, and S. Mittler-Neher, Adenin–uridin base pairing at the water-solid-interface, J. Am. Chem. Soc. 122, 87–95 (2000). 86. A. Theis, B. Menges, S. Mittler, M. Mierzwa, T. Pakula, and H. Ritter, Polymeric mesoions: Novel synthetic methods, photochemistry, and characterization in the solid state by dielectric and waveguide-mode spectroscopy, Macromolecules 36, 7520–7526 (2003). 87. X. Mai, R.S. Moshrefzahdeh, U.J. Gibson, G.I Stegeman, and C.T. Seaton, Simple versatile method for fabricating guided wave gratings, Appl. Opt. 24, 3155–3161 (1985). 88. S. Busse, V. Scheumann, B. Menges, and S. Mittler, Sensitivity studies for specific binding reactions using the biotin/streptavidin system by evanescent optical methods, Biosens. Bioelectron. 17, 704–710 (2002). 89. T. Liebermann, W. Knoll, P. Sluka, and R. Herrmann, Complement hybridization from solution to surface-attached probe-oligonucleotides observed by surfaceplasmon-field enhanced fluorescence spectroscopy, Colloids Surf. A 169, 337–350 (2000). 90. X.D. Su, R. Robelek, Y.J. Wu, G.Y. Wang, and W. Knoll, Detection of point mutation and insertion mutations in DNA using a quartz crystal microbalance and MutS, a mismatch binding protein, Anal. Chem. 76, 489–494 (2004).
46
Silvia Mittler and Bernhard Menges
91. D. Kambhampati, P.E. Nielsen, and W. Knoll, Investigating the kinetics of DNA– DNA and PNA–DNA interactions using surface plasmon resonance-enhanced fluorescence spectroscopy, Biosens. Bioelectron. 16, 1109–1118 (2001). 92. Y.T. Long, C.Z. Li, T.C. Sutherland, H.B. Kraatz, and J.S. Lee, DNA mismatch detection on gold surface by electrochemical impedance spectroscopy, Abstr. Pap. Am. Chem. Soc. 227: U88–U88 063-ANYL Part 1 (2004). 93. B. Dubertret, M. Calame, and A.J. Libchaber, Single-mismatch detection using gold-quenched fluorescent oligonucleotides, Nature Biotechnol. 19, 365–370 (2001). 94. M.T. van Os, B. Menges, R. Förch, R.B. Timmons, G.J. Vancso, and W. Knoll, Thin film plasma deposition of allylamine effects of solvent treatment, Mater. Res. Soc. Symp. Proc. 544, 45–50 (1999). 95. V. Jacobsen, B. Menges, R. Förch, S. Mittler, and W. Knoll, In-situ thin film diagnostics using waveguide mode spectroscopy, Thin Solid Films 409, 185–193 (2002). 96. V. Jacobsen, B. Menges, A. Scheller, R. Förch, S. Mittler, and W. Knoll, In situ film diagnostics during plasma polymerization using waveguide mode spectroscopy, Surf. Coat. Technol. 142–144, 1105–1108 (2001). 97. J.A. Forrest and K. Dalnoki-Veress, The glass transition in thin polymer films, Adv. Colloid Interface Sci. 94, 167–196 (2001). 98. J.A. Forrest, K. Dalnoki-Veress, J.R. Stevens, and J.R. Dutcher, Effect of free surfaces on the glass transition temperature of thin polymer films, Phys. Rev. Lett. 77, 2002 (1996). 99. J.A. Forrest, K. Dalnoki-Veress, and J.R. Dutcher, Interface and chain confinement effects on the glass transition temperature of thin polymer films, Phys. Rev. E 56, 5705– 5716 (1997). 100. W.E. Wallace, J.H. van Zanten, and W.L. Wu, Influence of an impenetrable interface on a polymer glass transition temperature, Phys. Rev. E 52, R3329–R3332 (1995). 101. Y. Grohens, M. Brogly, C. Labbe, M.-O. David, and J. Schultz, Glass transition of stereoregular poly(methyl methacrylate) at interfaces, Langmuir 14, 2929–2932 (1998). 102. J.K. Keddie, R.A.L. Jones, and R.A. Cory, Size dependent depression on the glass transition temperature in polymer films, Europhys. Lett. 27, 59 (1994). 103. S. Kawana and R.A.L. Jones, Character of the glass transition in thin supported films, Phys. Rev. E 63, Art. No. 021501 (2001). 104. K. Dalnoki-Veress, J.A. Forrest, C.X. Murray, C. Gigault, and J.R. Dutcher, Molecular weight dependence of reductions in the glass transiton temperature of thin, freely standing polymer films, Phys. Rev. E 63, Art.No. 031801 (2001). 105. H. Bock, S. Christian, W. Knoll, and J. Vydra, Determination of the glass transition temperature of nonlinear optical planar polymer waveguides by attenuated total reflection spectroscopy, Appl. Phys. Lett. 71, 3643 (1997). 106. O. Prucker, S. Christian, H. Bock, J. Rühe, C.W. Frank, and W. Knoll, On the glass transition in ultrathin polymer films of different molecular architecture, Macromol. Chem. Phys. 199, 1435–1444 (1998). 107. R. Kügler and W. Knoll, Influence of the polymethacrylate chain formation in Langmuir-Blodgett-Kuhn films on the glass transition temperature, Macromol. Chem. Phys. 203, 923–930 (2002).
2. Evanescent Waves as Nanoprobes
47
108. K. Dalnoki-Veress, J.A. Forrest, P.G. de Gennes, and J.R. Dutcher, Glass transition reductions in thin freely-standing polymer films: A scaling analysis of chain confinement effects, J. Phys. IV 10, 221–226 (2000). 109. P.G. de Gennes, Glass transitions in thin polymer films, Eur. Phys. J. E 2, 201–203 (2000). 110. G. Rehage and W. Borchard, in The Physics of Glassy Polymers, edited by R.N. Haward, Applied Intersciences, London (1973). 111. Polymer Handbook, 2nd edition, edited by J. Brandup and E.H. Immergut, Wiley, New York (1975). 112. H. Raether, Surface Plasmons, Springer, Berlin (1988). 113. G.W.H. Höhne, W.F. Hemminger, and H.-J. Flammersheim, Differential Scanning Calorimetry, Springer, Berlin (2003).
3 Porous Silicon Electrical and Optical Biosensors Huimin Ouyang, Marie Archer,12 and Philippe M. Fauchet1 Department of Electrical and Computer Engineering and Center for Future Health, University of Rochester, Rochester, NY 14627
3.1 Materials Science of Porous Silicon Porous silicon (PSi) is a form of silicon with unique properties, distinct from those of crystalline, microcrystalline, or amorphous silicon. It was first prepared in 1956 [1] and much later it was identified as etched silicon [2]. The most common fabrication technique to produce PSi is electrochemical etching of a crystalline silicon wafer in a hydrofluoric (HF) acid-based solution [3]. The electrochemical process allows for precise control of the structural properties of PSi such as thickness of the porous layer, porosity, and average pore diameter. The morphology of PSi is important for sensing applications because the pore diameter limits the size of the species that can be captured. PSi can be prepared with a wide range of optical and electrical properties which makes it a very flexible material. The internal surface of PSi is very large, ranging from a few to hundreds of square meters per gram [4]. Therefore, the properties of PSi are affected not only by its crystalline core and nanomorphology but also by its surface. In addition, the properties of the crystalline core differ from those of bulk c-Si, when the size of the silicon structures drops below 10 nm, a size regime in which quantum mechanical effects modify its electronic states [5, 6].
3.1.1 Control the Morphology and Porosity The dissolution of silicon requires the presence of fluorine ions (F− ) and holes (h+ ). The pore initiation and growth mechanisms are qualitatively understood. 1
Also with the Department of Biomedical Engineering, University of Rochester. Permanent address: U.S. Naval Research Laboratory, Center for Biomolecular Science and Engineering, Washington, DC 20375. 2
49
50
Huimin Ouyang, Marie Archer, and Philippe M. Fauchet
Pore growth can be explained by several models, each one of which is more relevant in a specific regime of porosity and pore size [7–9]. If the silicon/electrolyte interface becomes irregular shortly after etching starts, the surface fluctuations of the Si/electrolyte interface may either grow (PSi formation) or disappear (electropolishing). A depletion region is formed in the thin PSi layer itself and also in a region of the Si wafer near the PSi/c-Si interface. In forward bias for p-type substrates, the holes can still reach the Si/electrolyte interface as the electric field lines are focused at the tip of the pores. Thus, holes will preferentially reach the Si/electrolyte interface deep in the pores, where etching will proceed rapidly (Figure 3.1). In contrast, no holes will reach the end of the Si rods, effectively stopping the etching there. In addition, if this electrostatic effect is not strong enough, the random walk of the holes toward the Si/electrolyte interface makes it more likely that they reach it at or near the pore’s tip, resulting in an effect similar to the electrostatic one. When an n-type substrate is used, porous silicon formation takes place in reverse bias since holes are required for etching to proceed. Another important mechanism becomes predominant if the Si rods are narrow enough (typically much less than 10 nm). In this size regime, the electronic states start to differ from those of bulk silicon. When the motion of carriers is restricted in one or more dimensions, the holes in the valence band are pushed to lower energy by quantum confinement, which produces a potential barrier to hole transport from the wafer to the Si rods. The holes can no longer drift or diffuse into the Si rods and further etching stops. Pore formation occurs when the fluorine ions are delivered faster than the holes, the interpore regions of PSi are depleted of holes, and further etching occurs only at the pore tips. When the current density decreases, the number of holes at the pore tips drops, which leads to smaller pore sizes. Thus, the
Hydrofluoric Acid -
-
FF-
FF-
-
FF-
-
FF-
-
-
FF-
FF-
-
FF-
-
FF-
FF-
FF-
-
-
FF-
-
FF- FF-
FF-
+ ++ + + + +
FF-
-
FF-
-
FF-
-
FF-
+ ++ + +
Crystalline Silicon
+ +
F i g u r e 3.1. Schematic of PSi formation. Etching occurs only at the pore tips where the holes (h+ ) are focused by the electric field.
3. Porous Silicon Electrical and Optical Biosensors
51
90 80 70 Porosity (%)
60 50 40 30 20 10 0 0
10
20 Current density
30
40
50
(mA/cm2)
F i g u r e 3.2. Porosity as a function of etching current density. The data are obtained from highly doped n-type silicon using 5% HF etching solution.
porosity (defined as the percentage of void space in the material) can be precisely controlled by the etching current density. Figure 3.2 shows the dependence of the porosity on current density for highly doped n-type (0.01 ohm-cm) silicon [10]. Similar curves can be found on other types of substrates [9]. The pore morphology is strongly affected by the choice of doping type and concentration, as illustrated in Figure 3.3 [11]. The top-row figures are top-view SEM images of porous silicon samples with different pore diameters ranging from mesopores (pore size >10 nm, < 50 nm) to macropores (pore size >50 nm). The bottom-row figures are cross sectional SEM images of the same samples. The mesopores formed in p+ silicon substrates have very branchy pore walls (Figure 3.3a, b). These pores only allow the detection of small objects such as short DNA segments and chemicals. The macropores formed in n-type wafers (Figure 3.3c–h) have much smoother pore walls and larger pore sizes than the mesopores. They are suitable for the detection of macromolecules and even very large objects such as bacteria or viruses. Note that most mesoporous silicon samples and certainly all microporous silicon samples (pore sizes < 10 nm) exhibit strong luminescence in the visible to near-infrared region [12]. This results from quantum confinement of electrons and holes in nanometer-sized quantum structures, which increases the band gap [5, 6] and enhances the radiative recombination rate [13].
3.1.2 Control of the Physical Properties As already mentioned, the optical and electrical properties of PSi can be tuned by changing various parameters. The most spectacular effect is the tuning of the
200 nm
200 nm
f
200 nm
e
h
2 µm
2 µm
g
F i g u r e 3.3. (a, b) Top-view and cross-sectional SEM images of mesoporous silicon with an average pore diameter of approximately 20 nm. It is formed in highly doped p-type silicon (0.01 ohm-cm) using an electrolyte with 15% HF in ethanol. (c, d) SEM images of 60 -nm macropores formed in very highly doped n-type silicon (0.001 ohm-cm) using an electrolyte with 6% HF. (e, f) SEM images of 120-nm macropores formed in highly doped n-type silicon (0.01 ohm-cm) using an electrolyte with 6% HF. (g, h) SEM images of 1.5-m macropores etched from low-doped p-type silicon (20 ohm-cm) using an HF/dimethylformamide electrolyte.
200 nm
dd
200 nm
20 nm
bb
c
a
3. Porous Silicon Electrical and Optical Biosensors
53
luminescence from the band gap of bulk silicon to the UV by decreasing the size of the silicon remnants [12, 14]. The average size of the silicon remnants can be reduced to less than 2 nm by controlling the etching conditions (typically, by increasing the porosity) or by a postetching treatment (for example, oxidation). In this size regime, quantum-mechanical effects become important and modify the electronic states [13]. Quantum confinement increases the band gap and shifts the luminescence to shorter wavelengths, as shown in Figure 3.4 [14]. Immediately after etching, the internal surface of PSi is covered by silicon hydride bonds that produce an excellent surface passivation and, in the case of microporous silicon, strong luminescence. However, the luminescence of freshly etched PSi degrades quickly because the Si-H bonds can easily be broken, leading to dangling bonds that form nonradiative recombination centers [15]. It is thus useful to passivate the internal surface of PSi with SiO2 . This can be accomplished by various techniques, such as furnace oxidation or exposure to hydrogen peroxide. The stability of the luminescence efficiency of PSi passivated by SiO2 has been shown to be excellent [16]. The development of biosensors using oxide-passivated PSi is also facilitated as the wealth of knowledge on the interface between glass and biological matter can be explored. The electrical properties of PSi also differ strongly from those of bulk silicon [17]. Figure 3.5 shows results from time-of-flight measurements performed on oxidized PSi [18]. These results suggest that transport in this type of PSi is more similar to transport in a-Si:H than in crystalline Si. The results are consistent with a model that invokes transport on a fractal. Other transport mechanisms
4 Excitonic bandgap lowest e/h energy levels (assume si=o) In Air In Ar
3.5
Gap (eV)
Zone 3
Zone 2
Zone 1
3
2.5
2
1.5
1
1.5
2
2.5 3 Diameter (nm)
3.5
4
F i g u r e 3.4. Calculated excitonic band gap for silicon quantum dots of different sizes. When one Si-H passivating bond is replaced by a Si=O bond, the gap does not increase as fast when the diameter decreases. The data points show photoluminescence measurements performed in argon and in air.
54
Huimin Ouyang, Marie Archer, and Philippe M. Fauchet
F i g u r e 3.5. Drift mobility measured on an oxidized PSi pin diode structure as a function of temperature for a given ratio L/E of the carrier displacement over the applied electric field. The circles correspond to electron transport and the triangles to hole transport. The solid line shows data obtained for holes in a-Si:H.
may be in play as the connectivity of the porous structure and the average size of the silicon remnants change [17]. As we will discuss in the next section, the electrical properties of PSi, such as the conductivity, are also strongly influenced by environmental conditions, including adsorption of molecules or the presence of a fluid inside the pores. In contrast to the situation with optical properties, where a broad consensus has built over time and led to robust models, the electrical properties of PSi remain relatively poorly understood.
3.2 Electrical Biosensors The electrical properties of PSi are strongly influenced by the environment as evidenced by the large changes in conductivity [19–21] observed when the porous layer is infiltrated with organic solvents or exposed to molecules. At least two response mechanisms have been proposed to explain this behavior. The first mechanism suggests that charge redistribution takes place in the crystallites as a result of the alignment of polar molecules on the surface [22, 23]. This mechanism will be described in the following section and used to explain the electrical sensing principle of our sensor. In the second mechanism, oxidation and adsorption of molecules produce charge transfer reactions facilitated by the presence of surface traps [23, 24]. The second mechanism is also supported by observations made on mesoporous silicon in which exposure to valence band and conduction band quenchers with different redox potentials produces a shift in the photoluminescence (PL) peak [25]. Changes in capacitance and conductance of PSi have been widely used as transduction mechanisms in various sensing situations [22,23,26–33], but limited
3. Porous Silicon Electrical and Optical Biosensors
55
work has been done in the field of biological electrical sensors. Different electrode configurations have been reported to measure the changes in electrical properties of PSi. In the most common situation, metal contacts are evaporated on the PSi surface [34] with various configurations such as interdigitated and coplanar electrodes [24, 35, 36] or in a top and bottom (“sandwich”) configuration [22, 23, 33]. If the electrodes are in contact with the solvent or the buffer, the device characteristics may change over time as degradation at the contact electrodes is likely. Therefore, the electrodes need to be protected. An alternative geometry consists of using backside coplanar electrodes placed on the c-Si substrate and rely on the propagation of the electric field from the c-Si substrate to the PSi layer [37]. In this case the influence of the surface/metal contact barrier and any chemical reaction between the sensing species and the surface of the porous layer is eliminated. The response of these sensors is therefore related to the interaction of the sensing species and the PSi surface and can be explained with a Space Charge Region Modulation (SCRM) model.
3.2.1 Sensing Principle Figure 3.6 shows a schematic representation of the PSi electrical sensor with backside contacts connected to a computer-controlled LCR meter. When the porous layer is infiltrated with different liquids, a change in the baseline capacitance (C) and conductance (G) can be measured in real time. The sensor can be modeled as a field effect transistor (FET) in which the metal gate is substituted by the porous layer that acts as a chemical gate. The sensing principle is explained on the basis of the SCRM model [37]. When the surface of the porous layer is exposed to a solution, the liquid/solid interface tends to reach electrostatic equilibrium by modifying the space charge region in the PSi walls. An electrical double layer is formed between the space charge region (silicon) and the Helmholtz layer, which is sensitive to the adsorption/desorption of ions and the components of the liquid. Changes in the Helmholtz layer lead to a
F i g u r e 3.6. Schematic of a PSi electrical sensor with the backside contacts connected to a computer-controlled LCR meter.
56
Huimin Ouyang, Marie Archer, and Philippe M. Fauchet
modification of the space charge region in the silicon walls as a new electrostatic equilibrium is reached. According to the model, adsorbed molecules will change the space charge region of the PSi walls and the underlying c-Si substrate. Since the doping of the substrate is relatively low, a small change of the surface charge has a strong influence on the depletion region width. The degree to which this change occurs will depend on the physical properties of the adsorbed molecule (e.g., dipole moment, polarizability). After infiltration with a liquid, the porous layer behaves as a charged layer that modifies the field distribution in the whole structure (PSi/c-Si). This change in the electric field distribution of the structure is measured in real time as a change in capacitance (C) and conductance (G) and the device can be modeled with the simplified equivalent electrical circuit shown in Figure 3.7. The porous layer is represented by two RC components, one for the pores, which changes with the dielectric constant of the liquid, and another for the pore walls, which is related to changes in the depletion layer induced by the adsorption of molecules. The c-Si substrate is represented by a variable conductance that changes depending on the charge redistribution in the walls of the porous layer. From the point of view of an FET, the variable c-Si conductance represents the channel conductance.
3.2.2 Flow-Through Sensor Fabrication A flow-through biosensor would be more desirable than the biosensor configuration shown in Figure 3.6, as larger volumes of liquid can be passed through the sensor, leading to increased response speed and enhanced sensitivity [38, 39].
F i g u r e 3.7. Schematic representation of the cross section of the PSi sensor and the electrical equivalent circuit with the associated capacitive and conductive components.
3. Porous Silicon Electrical and Optical Biosensors
57
A schematic representation of a flow-through device structure is shown in Figure 3.8. This sensor configuration isolates the contacts, and, potentially, microelectronics circuitry from the backside fluidics. Note that the contact regions are not within the flow-through regions of the membrane. A protecting layer (i.e., SiO2 , polyimide) can be easily patterned over the metal electrodes to avoid topside interaction with fluids. The lateral extension of the PSi beyond the contact regions minimizes the shunt conductance through the silicon substrate. The V-groove produced by KOH etching can extend over an array of devices, but the lateral etching of the PSi membrane beyond the mask edge presents scaling limitations. Macroporous silicon electrical sensors were fabricated using an electrolyte with 4 wt% hydrofluoric acid (49 wt%) in N N -dimethylformamide (DMF). The use of a mild oxidizer such as DMF with low-doped silicon results in very straight pore walls and pore diameters between 1 and 2 m [40]. The membranes were etched to a depth of approximately 70 m using silicon nitride as an etch mask. Another nitride mask was defined on the backside of the wafer (aligned to the front) and a KOH etch was used to form a deep cavity, providing fluidic delivery to the free-standing membrane. With this procedure, an overetch can be used to compensate for pore depth nonuniformity due to current-crowding effects during the electrochemical etching process. Finally, the structure was thermally oxidized, providing a SiO2 layer approximately 1000 Å thick within
P-type substrate
(a) PSi sensing membrane
Electrode masking oxide
(b) KOH backside V-groove etch
F i g u r e 3.8. Layout (a) and cross section (b) of an integrated PSi-based flow-through sensor device. The dashed line across (a) shows the cut –line for the cross section in (b).
58
Huimin Ouyang, Marie Archer, and Philippe M. Fauchet
F i g u r e 3.9. SEM cross sections of the macroporous silicon flow-through sensing membrane. The background image is a magnification of the inset on the left. The PSi layer was etched to a depth ∼ 50 m. The KOH backside etch continued beyond the intersection with the porous layer. Pore liners of silicon dioxide and silicon nitride remain suspended beneath the remaining 20-m-thick PSi membrane.
the macropores. Figure 3.9 shows SEM cross sections of a membrane structure that has been overetched considerably. Note that in areas where the membrane has been thinned, the protecting liners remain as suspended stalactites.
3.2.3 Chemical Sensing Capacitance (C) and conductance (G) measurements were performed with both PSi layers attached to the substrate and flow-through membranes. Real-time data acquisition and storage was done using a PC control interfaced with LabViewTM . The measurements were performed at 10 to 100 kHz and 0 V DC bias. The device chips were placed into the test fixture of the LCR meter, channel side up, and a baseline capacitance measurement was taken. The sensors were exposed to many different solvents, including chloroform, acetone, ethanol, methanol, toluene, IPA, and acetonitrile. Since the sensors are sensitive to changes in the ambient conditions such as relative humidity, temperature, and light, these parameters were monitored during testing to ensure that the device response was exclusively from the analyte. Figure 3.10 shows a real-time measurement of the capacitance, taken when approximately 30 L of solvent was introduced in a sequential manner in the center of the channel, filling the channel and sensing membrane [41]. Each solvent exhibits a characteristic signature (amplitude, sign, shape, duration). Each of these features is related to the different physical properties of the solvent such as vapor pressure, dipole
3. Porous Silicon Electrical and Optical Biosensors
59
F i g u r e 3.10. Characteristic signatures of five solvents tested sequentially in a flowthrough sensor. Each signature is unique to the specific solvent, with distinctive features (shape, duration). Although there is a baseline drift, the response signatures are virtually identical to those taken with sensors dedicated to a single solvent.
moment, dielectric constant, and polarizability. Water and nonpolar solvents exhibit a different response which can be used to identify each of them [37]. After exposure to toluene, the sensor permanently loses its sensitivity. A demonstration of the repeatability and reproducibility of the sensors is shown in Figure 3.11.
F i g u r e 3.11. Successive tests with methanol on the same sensor.
60
Huimin Ouyang, Marie Archer, and Philippe M. Fauchet
3.2.4 Biological Sensing Since the device is sensitive to the presence of charged molecules and changes in the dielectric constant, biological events, such as DNA hybridization, can be detected in real time. When several molecules of single-stranded DNA are infiltrated into the porous layer, they can be adsorbed on the surface through electrostatic interactions. These DNA single strands are used as probes that can capture a complementary strand. Hybridization produces an increase in the overall charge hence a change in the depletion region width. The PSi sensors demonstrated sensitivity to DNA hybridization, with capacitance measurements showing a clearly recognizable signal. Figure 3.12 shows the normalized values of capacitance for a binding and a nonbinding event [38]. The first rise in the signal corresponds to the infiltration of the probe DNA (pDNA) and the second one to the hybridization signal when the complementary sequence is added (cDNA). When the pDNA sequence in Hepes buffer or NaCl is infiltrated into the pores, it will attach to the porous surface. The thin oxide layer on the surface allows the modification of the depletion layer leading to a change in capacitance. As the NaCl buffer displaces the air inside the pores, the change in dielectric constant will contribute to the capacitance signal. When DNA hybridizes, the charge effect is enhanced, thereby producing a rise in the signal above the one produced by the probe DNA (pDNA). The principle of detection of the device is based on the simultaneous effect of a change in dielectric constant and a modulation of the depletion layer of the structure resulting from the presence of charged molecules, in agreement with the model of Section 3.2.1. To assess the selectivity of the device we performed the same
F i g u r e 3.12. Normalized values of capacitance upon binding of the probe DNA (pDNA) and the complementary sequence (cDNA). The selectivity of the device is demonstrated by exposing pDNA to a noncomplementary sequence (ncDNA).
3. Porous Silicon Electrical and Optical Biosensors
61
experiment with a noncomplementary sequence. In this case, although a signal is produced, the change in C when the noncomplementary DNA (ncDNA) is infiltrated is significantly less (∼10%) than the one induced when binding occurs (∼40%). The effect of the charge of DNA alone on the response of the PSi sensors can be examined by using an uncharged analog of DNA known as peptide nucleic acid (PNA). Since PNA is composed of the same bases as DNA, it hybridizes to DNA but hybridization should not produce the same charge effect. Experimental results support this prediction. When PNA and DNA hybridize, the measured signal was found to be identical to that measured when a noncomplementary DNA strand is introduced into the pores [42]. Mass and charge effects on the response of the sensor were also studied by performing various control experiments. For instance, while the infiltration of the buffer itself produces a change in impedance and phase angle, the magnitude is significantly different from that of the binding event. In this specific case the response is also produced by the adsorption of the buffer components on the surface as well as a change in the dielectric constant of the pores.
3.3 Optical Biosensors PSi is a good host material for label-free optical biosensing applications because its optical properties (photoluminescence, reflectance) are highly sensitive to the presence of chemical and biological species inside the pores [43]. PSibased affinity optical biosensors with a variety of configurations such as single layer Fabry-Perot cavities [44], Bragg mirrors [45], rugate filters [46], and microcavities [47–49] have been experimentally demonstrated for the detection of toxins [50], DNA [47], and proteins [10, 44]. The capture of biological or chemical molecules inside the pores increases the effective refractive index of the PSi structures thus causing a red shift in the photoluminescence or reflectance spectra.
3.3.1 Sensing Principle The effective dielectric constant of a PSi layer is related to its porosity by the Bruggeman effective medium model [11]:
1 − P
− PSi Si − PSi + P void =0 Si + 2PSi void + 2PSi
(3.1)
where P is porosity, PSi is the effective dielectric constant of porous silicon, Si is the dielectric constant of silicon, and void is the dielectric constant of the medium inside the pores. The Bruggeman effective medium model shows that the effective refractive index of PSi (neff 2 = PSi ) increases as the porosity
62
Huimin Ouyang, Marie Archer, and Philippe M. Fauchet
decreases and as void increases. In Figure 3.13, neff is plotted as a function of porosity [10]. In sensing applications, void increases due to the binding of targets to the internal surface of the pores. Thus, the overall effective dielectric constant of the porous structure PSi increases which causes a red shift in the optical reflectance spectrum of the structure. As shown in Figure 3.13, for a given increase of void , the effective refractive index change is larger for higher porosity layers. In order to selectively detect targets of interest, the internal surface of PSi needs to be functionalized. Highly selective elements, such as DNA segments and antibodies, can be immobilized on the internal surface of the pores as the bioreceptors or probe molecules. When the sensors are exposed to the target, the probe molecules selectively capture the target molecules. The molecular recognition events are then converted into optical signals via the increase of the refractive index. A PSi microcavity is a one-dimensional photonic band gap structure that contains a defect (symmetry breaking) layer sandwiched between two Bragg mirrors [51]. Each Bragg mirror is a periodic stack of layers with two different porosities and quarter wavelength optical thickness. The schematic drawing of a PSi microcavity and its typical reflectance and photoluminescence spectra are shown in Figure 3.14. Depending on the thickness of the defect layer, the reflectance spectrum of a microcavity is characterized by one or several sharp resonance dips in the stop band. The reflectance spectrum modulates the measured PL spectrum and produces one or several very narrow PL peaks. The position of the reflectance dip or photoluminescence peak is determined by the optical thickness (refractive index times the physical thickness) of each layer in the structure. A slight change of the refractive index inside the pores causes a shift of the spectrum.
4 n-void=1 n-void=1.3
3.5
neff
3 2.5 2 1.5 1 0
20
40
60
80
100
Porosity (%)
F i g u r e 3.13. Effective refractive index of PSi as a function of the porosity at the wavelength of 800 nm. The black curve corresponds to nvoid = 1 and the gray curve to nvoid = 13.
3. Porous Silicon Electrical and Optical Biosensors
0.8 0.6 0.4
PSi Microcavity
0.6 0.4 0.2
0.2 Si Substrate
c
0.8
PL (a.u.)
Reflectance
1
b
1
a
63
0
0 0.6
0.7
0.8
0.9
Wavelength (µm)
1
0.7
0.8
0.9
Wavelength (µm)
F i g u r e 3.14. (a) Schematic of a PSi microcavity. (b) Simulation of the reflectance spectrum of a PSi microcavity with a half-wavelength optical thickness defect layer and 6-period Bragg mirrors. (c) Simulation of the PL spectrum of the same microcavity.
3.3.2 Microcavity Sensor Design and Sensitivity The figure of merit describing the sensitivity of affinity sensors is /n, where is the wavelength shift and n is the change of the ambient refractive index. For a PSi microcavity sensor with an average porosity of 75%, /n is ∼ 550 nm [52], which is much larger than for sensing platforms that rely on the interaction between the evanescent tail of the field and the analyte [53]. For a system able to detect a wavelength shift of 0.1 nm, the minimum detectable refractive index change of the pores is 2 × 10−4 . The sensitivity of PSi microcavity sensor can be increased by increasing its Q-factor (Q = / , where is the resonance center wavelength and is the full width half maximum of the resonance dip). For higher Q-values, the spectral features are sharper and smaller shifts can be detected. The Q-factor can be increased by increasing the contrast in the porosity of the layers. However, a higher contrast in porosity is usually produced by a higher contrast in pore opening, which may not be favorable for biosensing applications when easy infiltration of the target throughout the entire multilayer structure is required. For a given porosity contrast, the Q-factor can also be increased by increasing the number of periods of the Bragg mirror. In practice, the number of periods cannot be increased arbitrarily for two reasons. First, uniform infiltration of the molecules becomes more difficult in thicker devices. Second, maintaining a constant HF concentration at the tip of very deep pores is difficult [54], which may lead to an undesired porosity or refractive index gradient. PSi-based PBG sensors also have the advantage of size exclusion. When the PSi sensor is exposed to a complex biological mixture, only the molecules that are smaller than the pores can be infiltrated into the sensor. Furthermore, an increase of refractive index on the top of the microcavity due to the nonspecific binding of large size unwanted objects only causes changes to the side lobes in the reflectivity spectrum, not to the resonance dip [55]. Thus, PSi microcavities are more reliable than planar sensing platforms, where the nonspecific binding of large-size objects present in a “dirty” environment may produce a false-positive signal.
64
Huimin Ouyang, Marie Archer, and Philippe M. Fauchet
The pore size also affects the sensitivity of PSi biosensors because in biosensing applications, the target does not completely fill the pores but instead is attached to the pore walls. For a PSi layer of a given porosity, the internal surface area decreases as the pore size increases. The effective refractive index change of a layer with larger pores is thus smaller since the percentage of the pore volume occupied by the biological species is smaller. We simulated the spectra for microcavities with fixed porosities (80% for the high-porosity layer and 70% for the low-porosity layer) but different pore diameters ranging from 20 nm to 180 nm. For a given thickness of the coating (with nlayer = 142, a typical value for biomolecules), the resonance red shift decreases as the pore size increases, as shown in Figure 3.15 [10]. It can be seen that, for a 1-nm-thick coating layer, a microcavity with 40-nm pores produces a red shift of 23 nm, while a microcavity with 100-nm pores gives a red shift of only 10 nm. Thus, to optimize the sensitivity, the pore size should be as small as possible while still allowing for easy infiltration of the biological material. From Figure 3.15 we can also estimate the areal mass sensitivity in terms of gram/internal surface area. We assume a detection system able to resolve a shift of 0.1 nm. For a microcavity with 20-nm pores, the minimum coating thickness required to achieve a detectable signal is 0.002 nm, which is equivalent to ∼ 2 pg/mm2 . For a microcavity with 180-nm pores, the minimum coating thickness is 0.02 nm, which is equivalent to ∼ 20 pg/mm2 .
A
B
8
L = 1 nm L = 0.7nm L = 0.5nm L = 0.3 nm L = 0.1 nm L = 0.05 nm
7 Red shift (nm)
6 5 4 3 2 1 0 0
50
100 150 Pore diameter (nm)
200
F i g u r e 3.15. Simulation of microcavity spectrum red shift as a function of pore size. Each curve represents a different thickness (L) of the coating layer with n = 142. The porosities of the layers used in all the calculations were fixed at 80% and 70%. For a given thickness of the coating (shaded area), the effective refractive index change of a layer with small pores (A) is higher than that of a layer with large pores (B), which causes a larger shift in the spectrum. For a given pore size, the thicker the coating, the larger the shift.
3. Porous Silicon Electrical and Optical Biosensors
65
3.3.3 Fabrication of PSi Microcavity The porosity can be controlled by the etching current density. Once a layer has been etched, further etching using a different current density does not affect it as explained in Section 3.1.1. Stacks of layers with different refractive indices can thus be formed by alternating the current density during etching [56]. Figure 3.16 shows a cross-sectional SEM image of a multilayer structure etched by a periodic current density pulse train. Each specific current density produces a different porosity. The duration of current density determines the thickness of the layer. By controlling the current density and etching time, layers with the proper optical thickness can be formed. Figure 3.17 shows cross-sectional and top-view SEM images of two different types of microcavities with different pore sizes. The mesoporous silicon microcavity with pore diameters from 10 nm to 50 nm was fabricated from a p+ wafer (0.01 ohm-cm) with 15% HF in ethanol. The macroporous silicon microcavity with pore diameters from 80 nm to 150 nm was etched in an n+ wafer (0.01 ohm-cm) with 5.5% HF in DI water [10]. The mesoporous microcavity is a good option for detection of small-size targets such as short DNA strands, while the macroporous microcavity is suitable for macromolecule sensing.
3.3.4 Biological Sensing 3.3.4.1 DNA Detection Mesoporous silicon microcavities were investigated for the detection of small DNA segments (22 based pairs) [47, 57]. Strong photoluminescence is observed from the mesoporous silicon microcavity. Multiple photoluminescence peaks as narrow as 3 nm of full width half maximum (FWHM) were measured from a microcavity with thick defect layer. The first step in the sensor preparation mA/cm2
J
j1 j2 Time
j1 j2 j1
500 nm
a. a
b
F i g u r e 3.16. (a) Cross-sectional SEM image of a PSi multilayer structure formed by a periodic current pulse train. The porosity and thickness of each layer are determined by the current density amplitude and duration, respectively. (b) Schematic drawing of the etching current density over time.
66
Huimin Ouyang, Marie Archer, and Philippe M. Fauchet 100
b Reflectance (%)
a
c
80 60 40 20 0 600
2 µm
200 nm
d
700
800
900
Wavelength (nm) 100
Reflectance (%)
e
f
80 60 40 20 0 600
200 nm
2 µm
700
800
900
Wavelength (nm)
F i g u r e 3.17. (a, b) Top-view and cross-sectional SEM images of a mesoporous silicon microcavity with pore sizes from 10 nm to 50 nm. (c) Reflectance spectrum of a similar mesoporous silicon microcavity. (d, e) Top-view and cross-sectional SEM images of a macroporous silicon microcavity with pore size from 80 nm to 150 nm. (f) Reflectance spectrum of the same macroporous silicon microcavity.
involves the silanization of the thermally oxidized porous silicon sample with 3-glycidoxypropyltrimethoxy silane, which is hydrolyzed to a reactive silanol by using DI water (pH ∼4). The thermal oxidation treatment not only produces a silica-like surface, but also improves the photo-stability of luminescent porous silicon film (see Section 3.1.2). After successful silanization, the probe DNA, which has an amine group attached to the 3 end of the sequence, is immobilized onto the pore surface via diffusion. The amine group attacks the epoxy ring of the silane, thereby opening it up and forming a bond. Finally, the DNA attached porous silicon sensor is exposed to the complementary strand of DNA (cDNA). Comparing the photoluminescence spectrum of the sensor before and after the DNA hybridization, a red shift can be detected due to the DNA/cDNA binding as shown in Figure 3.18 [47]. The detection limit of the sensor was determined to be in the picomolar range. 3.3.4.2 Gram-Negative Bacteria Detection To detect gram-negative bacteria, it is first necessary to select a target molecule present in this bacterial subclass and not in gram-positive bacteria. Lipopolysaccharide (LPS) is a primary constituent of the outer cellular membrane of gramnegative bacteria [58]. The precise structure of LPS varies among bacterial species but overall it is composed of three parts: a variable polysaccharide chain, a core sugar, and lipid A. As lipid A is common to all LPS subtypes, this seems a natural target. An organic receptor, tetratryptophan ter-cyclopentane (TWTCP), was designed and synthesized as the probe molecule. TWTCP specifically binds to diphosphoryl lipid A in water with a dissociation constant of 592 nm [59].
3. Porous Silicon Electrical and Optical Biosensors
67
Normalized PL Intensity (a.u.)
(a) PSi / DNA
(b) PSi / DNA / cDNA
(c) Differential Signal
600
650
700 750 800 Wavelength (nm)
850
900
F i g u r e 3.18. (a) PL spectrum of a mesoporous silicon microcavity with probe DNA (50 M) immobilized inside the device. (b) PL spectrum of the microcavity after exposure to cDNA (1 M). (c) Differential PL spectrum.
After the mesoporous silicon microcavity sensor is treated with 3-glycidoxypropyltrimethoxy silane, a mixture of TWTCP and glycine methyl ester is applied to the sensor. Glycine methyl ester is used as blocker molecules to avoid the reaction of the four amino groups of the tetratryptophan receptor with the epoxide-terminated PSi surface. As shown in Figure 3.19, upon exposure of lysed gram-negative cells (Escherichia coli) to the immobilized TWTCP sensor, a 4nm red shift of the photoluminescence spectrum of the microcavity is detected [60]. However, when the sensor is exposed to a solution of lysed gram-positive cells (Bacillus subtilis), no shift of the spectrum is observed. These results were confirmed with all gram-negative and gram-positive bacteria tested. 3.3.4.3 Protein Sensing Mesoporous silicon microcavities are better suited for the detection of small objects. For large size protein detection, macroporous silicon microcavities are a better option because they allow much easier infiltration of large molecules such as immunoglobulin G (IgG). A protein biosensor based on a macroporous silicon microcavity was demonstrated with the streptavidin–biotin couple [10]. While biotin is a small molecule, streptavidin is relatively large (67 kDa), making its infiltration difficult into mesopores but easy into macropores. Furthermore, each streptavidin tetramer has four equivalent sites for biotin (two on each side of the complex), which makes it a useful molecular linker. To create a biotin-functionalized sensor for the capture of streptavidin, the microcavity was first thermally oxidized, then silanized with aminopropyltriethoxysilane to create amino groups on the internal surface. The probe molecules,
Huimin Ouyang, Marie Archer, and Philippe M. Fauchet 1 0.9 0.8 0.7 0.6 0.5 0.4 0.3 0.2 0.1 0
Intensity
Intensity
68
775 875 Wavelength (nm)
675
0.6
0.6
0.4
0.4
0.2
0.2
Intensity
Intensity
675
1 0.9 0.8 0.7 0.6 0.5 0.4 0.3 0.2 0.1 0
0 – 0.2
775 875 Wavelength (nm)
0
– 0.2 – 0.4
– 0.4 – 0.6 675
775 Wavelength (nm)
875
– 0.6 675
775
875
Wavelength (nm)
F i g u r e 3.19. Photoluminescence spectra of a mesoporous silicon microcavity biosensor in the presence and absence of bacterial cell lysates.(top) The spectra on the left show response to gram-positive bacteria, while the spectra on the right show response to gram-negative bacteria.(bottom) The traces at the bottom are the differential spectra.
sulfo-NHS-LC-LC-biotin [sulfosuccinimidyl-6-(biotinamido)-6-hexa-namido hexanoate], were then immobilized inside the pores. As shown in Figure 3.20a, the red shift of the resonance increases as the biotin concentration increases. Using the simulation discussed in Section 3.3.2, we can estimate the biotin surface coverage, which is linearly related to the red shift in Figure 3.20a. A 10-nm red shift corresponds to a nearly complete (95%) biotin surface coverage. To study how the biotin surface coverage affects the binding to streptavidin, sensors derivatized with different biotin concentrations were exposed to the same amount of the target: 50 l of streptavidin with a concentration of 1 mg/ml. After exposure to streptavidin, a red shift was detected which is attributed to the specific binding of streptavidin to the biotin-derivatized macroporous microcavity (Figure 3.20b). For the control samples that were silanized but did not contain biotin, no shift was detected after exposure to streptavidin, which indicates that nonspecific absorption of streptavidin inside the microcavity is nonexistent or negligible. The red shift caused by streptavidin binding to biotin is a function of the biotin surface coverage. Figure 3.20c shows that there is an optimum biotin surface coverage that maximizes the red shift, therefore the capture of streptavidin. This behavior is in good agreement with observations by other researchers using
3. Porous Silicon Electrical and Optical Biosensors (a)
100 Reflectivity (%)
∆λ (nm)
10 8 6 4 2 0 0
2 0.4 0.8 1.2 1.6 Biotin concentration (mg/ml)
20
(b)
12
(c)
80
16
∆λ (nm)
14
69
60 40
12 8 4
20 0 600 650 700 750 800 850 900
Wavelength (nm)
0
0
20
40
60
80
100
Biotin surface coverage (%)
F i g u r e 3.20. (a) Dependence of the red shift on the concentration of biotin applied on the sensor. (b) A 10-nm red shift is detected after the sensor is exposed to the target. The gray curve is the reflectance spectrum of the sensor with biotin. The black curve is the reflectance spectrum after the sensor is exposed to streptavidin (1 mg/ml). (c) Red shift due to specific binding of streptavidin as a function of the biotin surface coverage.
different sensing techniques [61]. The spacing between each neighboring biotin needs to be large enough so that biotin can reach the pocketlike binding site of streptavidin. The roll-off of the red shift shown in Figure 3.20c is due to the fact that when the biotin surface density becomes very high and each biotin is closely surrounded by its neighbors, biotin cannot protrude deep enough into the binding site of streptavidin, thus decreasing the probability of capturing streptavidin. 3.3.4.4 IgG Sensor IgG is the most common type of antibody synthesized in response to a foreign substance (antigen). The antibody has a specific molecular structure capable of recognizing a complementary molecular structure on the antigen which might be some proteins, polysaccharides, and nucleic acids. From the X-ray crystal structure, the longest dimension of IgG is approximately 17 nm [62]. The detection of rabbit IgG (150 kDa) was investigated through multiple layers of biomolecular interactions in a macroporous silicon microcavity sensor. The silanized sensor was first derivatized with biotin which can selectively capture streptavidin as described in the previous section. The immobilized streptavidin can be used as a linker because of its free binding sites. Exposure of biotinylated goat anti-rabbit IgG to the sensor results in its attachment to the surface through the binding between biotin and streptavidin. The sensor uses goat anti-rabbit IgG as the probe molecule to selectively capture rabbit IgG. A red shift of the spectrum can be detected when each layer of molecules is added to the sensor. As shown in Figure 3.21, when the sensor was exposed to 50 l of a solution containing rabbit IgG at a 1 mg/ml concentration, a 6-nm red shift was detected [52]. When the sensor was exposed to 50 l goat IgG (1 mg/ml) which does not bind to the goat anti-rabbit IgG, the red shift is extremely small (< 0.5 nm). This control experiment shows that the sensor can selectively detect rabbit IgG.
Huimin Ouyang, Marie Archer, and Philippe M. Fauchet
∆λ (nm)
70
8 7 6 5 4 3 2 1 0
Rabbit IgG
Goat IgG
F i g u r e 3.21. A 6-nm red shift of the spectrum is detected when the PSi microcavity sensor is exposed to the target molecule rabbit IgG. When the sensor is exposed to goat IgG, the red shift is extremely small.
3.4 Conclusions Biological and chemical sensors made of porous silicon have been designed, fabricated, and tested. They rely on the sensitivity of the electrical and optical properties of this material to environmental factors. Models have been proposed to explain and quantify the response of the sensors to various chemicals and biological matter, including DNA and proteins. The fact that they are fabricated in silicon suggests that single sensor elements and sensor arrays can be fabricated inexpensively and reliably. We believe that these sensors are useful as analytical tools as well as for point of care applications and for use by untrained individuals. Acknowledgments. This work was supported in part by grants from the U.S. National Science Foundation and the Infotonics Center of Excellence in Canandaigua, NY. The authors acknowledge the following individuals for their contributions: Professor B. Miller, Professor K. Hirschman, Dr. S. Chan, Dr. M. Christophersen, Dr. L. DeLouise, Dr. S. Horner, J. Clarkson, and R. Viard.
References 1. A. Uhlir, Jr., Bell Syst. Tech. J. 35, 333 (1956). 2. Y. Watanabe, Y. Arita, T. Yokoyama, and Y. Igarashi, J. Electrochem. Soc. 122, 1351 (1975). 3. P. M. Fauchet, in Encyclopedia of Applied Physics, Update 2, Wiley-VCH Verlag, pp. 249–272 (1999). 4. L. T. Canham, in Properties of Porous Silicon, edited by L. Canham, INSPEC, London, pp. 81–89 (1997). 5. L. T. Canham, Appl. Phys. Lett. 57, 1046 (1990). 6. V. Lehmann and U. Gosele, Appl. Phys. Lett. 58, 856 (1991). 7. R. L. Smith and S. D. Collins, J. Appl. Phys. 71, R1 (1992). 8. A. G. Cullis, L. T. Canham, and P. D. J. Calcott, J. Appl. Phys. 82, 909 (1997). 9. V. Lehmann, Electrochemistry of Silicon, Wiley-VCH Verlag, GmbH (2002).
3. Porous Silicon Electrical and Optical Biosensors
71
10. H. Ouyang, M. Christophersen, R. Viard, B. L. Miller, and P. M. Fauchet, Adv. Funct. Mater. 15, 1851 (2005). 11. W. Theiss, Surf. Sci. Rep. 29, 91 (1997). 12. P. M. Fauchet, in Light Emission in Silicon: From Physics to Devices, edited by D. J. Lockwood, Academic Press, San Diego, pp. 206–252 (1998). 13. M. S. Hybertsen, Phys. Rev. Lett. 72, 1514 (1994). 14. M. V. Wolkin, J. Jorné, P. M. Fauchet, G. Allan, and C. Delerue, Phys. Rev. Lett. 82, 197 (1999). 15. R. T. Collins, M. A. Tischler, and J. H. Stathis, Appl. Phys. Lett. 61, 1649 (1992). 16. L. Tsybeskov, S. P. Duttagupta, K. D. Hirschman, and P. M. Fauchet, Appl. Phys. Lett. 68, 2058 (1996). 17. A. J. Simons, in Properties of Porous Silicon, edited by L. Canham, INSPEC, London, pp. 163–184 (1997). 18. P. N. Rao, E. A. Schiff, L. Tsybeskov, and P. Fauchet, Chem. Phys. 284, 129 (2002). 19. C. Cadet, D. Deresmes, D. Villaume, and D. Stievenard, Appl. Phys. Lett. 64, 2827 (1994). 20. V. Lehmann, F. Hofmann, F. Moeller, and U. Gruning, Thin Solid Films 255, 20 (1995). 21. L. A. Balagurov, D. G. Yarkin, and E. A. Petrova, Mater. Sci. Eng. B 69/70, 127 (2000). 22. M. Ben-Chorin, A. Kux, and I. Schechter, Appl. Phys. Lett. 64, 481 (1994). 23. I. Schechter, M. Ben-Chorin, and A. Kux, Anal. Chem. 67, 3727 (1995). 24. S. Green and P. Kathirgamanathan, Mater. Lett. 52, 106 (2002). 25. J. Rehm, G.L. McLendon, and P.M. Fauchet, J. Am. Chem. Soc. 118, 4490 (1996). 26. G. Barillaro, A. Nannini, and F. Pieri, Sens. Actuat. B 93, 263 (2003). 27. S.-J. Kim, S.-H. Lee, and C.-J. Lee, J. Phys. D 34, 3505 (2001). 28. M. Thust, M. J. Schöning, S. Frohnoff, R. Arens-Fischer, P. Kordos, and H. Lüth, Meas. Sci. Technol. 7, 26 (1996). 29. M. Ben Ali, R.Mlika, H. Ben Ouada, R. M’ghaïeth, and H. Maâaref, Sens. Actuat. A 74, 123 (1999). 30. R. R. K. Reddy, A. Chadha, and E. Bhattacharya, Biosens. Bioelectron. 16, 313 (2001). 31. Z. M. Rittersma, W. J. Zaagman, M. Zetstra, and W. Benecke, Smart Mater. Struct. 9, 351 (2000). 32. S.-J. Kim, J.-Y. Park, S.-H. Lee, and S.-H. Yi, J. Phys. D 33, 1781 (2000). 33. A. Motohashi, M. Ruike, M. Kawakami, H. Aoyagi, A. Kinoshita, and A. Satou, Jpn. J. Appl. Phys. 35, 394 (1996). 34. R. C. Anderson, R. S. Muller, and C. W. Tobias, Sens. Actuat. A A21/A23, 835 (1990). 35. K. Watanabe, T. Okada, I. Choe, and Y. Sato, Sens. Actuat. B 33, 194 (1996). 36. S.-J. Kim, S.-H. Lee, and C.-J. Lee, J. Phys. D 34, 3505 (2002). 37. M. Archer, M. Christophersen, and P.M. Fauchet, Sens. Actuat. B 106, 347 (2005). 38. M. Archer, M. Christophersen, P. M. Fauchet, D. Persaud, and K. D. Hirschman, Mater. Res. Soc. Symp. Proc. 782, 385 (2004). 39. J. P. Clarkson, V. Rajalingam, K. D. Hirshman, H. Ouyang, W. Sun, and P. M. Fauchet, Mater. Res. Soc. Symp. Proc. 869, D321 (2005). 40. H. Foell, M. Christophersen, J. Carstensen, and G. Hasse, Mater. Sci. Eng. R39, 93 (2002).
72
Huimin Ouyang, Marie Archer, and Philippe M. Fauchet
41. J. P. Clarkson, P. M. Fauchet, V. Rajalingam, and K. D. Hirshman, IEEE Sensors Journal (to appear in March 2007). 42. M. Archer, M. Christophersen, and P.M. Fauchet, Biomed. Microdev. 6, 203 (2004). 43. M. P. Stewart and J. M. Buriak, Adv. Mater. 12, 859 (2000). 44. K.-P. S. Dancil, D. P. Greiner, and M. J. Sailor, J. Am. Chem. Soc. 121, 7925 (1999). 45. P. A. Snow, E. K. Squire, P. S. J. Russell, and L. T. Canham, J. Appl. Phys. 86, 1781 (1999). 46. F. Cunin, T. A. Schmedake, J. R. Link, Y.Y. Li, J. Koh, S. N. Bhatia, and M. J. Sailor, Nature Mater. 1, 39 (2002). 47. S. Chan, Y.Li, L. J. Rothberg, B. L. Miller, and P. M. Fauchet, Mater. Sci. Eng. C 15, 277 (2001). 48. L. Pavesi, Riv. Nuovo Cimento 20, 1 (1997). 49. H. Ouyang, M. Christophersen, and P. M. Fauchet, Phys. Status Solidi A 202, 1396 (2005). 50. H. Sohn, S. Letant, M. J. Sailor, and W. C. Trogler, J. Am. Chem. Soc. 122, 5399 (2000). 51. J. E. Lugo, H. A. Lopez, S. Chan, and P. M. Fauchet, J. Appl. Phys. 91, 4966 (2002). 52. H. Ouyang and P. M. Fauchet, Proc. SPIE 6005, 600508-1 (2005). 53. J. Scheuer, W. M. G. Green, G. A. DeRose, and A.Yariv, IEEE J. Sel. Top. Quantum Electron. 11, 476 (2005). 54. M. Thonissen, M. G. Berger, S. Billat, R. Ares-Fischer, M. Kruger, H. Luth, W. Theiss, S. Hillbrich, P. Grosse, G. Lerondel, and U. Frotscher, Thin Solid Films 297, 92 (1997). 55. H. Ouyang, L. A. DeLouise, M. Christophersen, B. L. Miller, and P. M. Fauchet, Proc. SPIE 5511, 71 (2004). 56. L. Pavesi, Riv. Nuovo Cimento 20, 1 (1997). 57. S. Chan, P. M. Fauchet, Y. Li, L. J. Rothberg, and B. L. Miller, Phys. Status Solidi A 182, 541 (2000). 58. L. S. Young, W. J. Martin, R. D. Meyer, R. J. Weinstein, and E. T. Anderson, Ann. Intern. Med. 86, 456 (1997). 59. R. D. Hubbard, S. R. Horner, and B. L. Miller, J. Am. Chem. Soc. 123, 5811 (2001). 60. S. Chan, S. R. Horner, P. M. Fauchet, and B. L. Miller, J. Am. Chem. Soc. 123, 11797 (2001). 61. L. S. Jung, K. E. Nelson, P.S. Stayton, and C.T. Campbell, Langmuir 16, 94221 (2000). 62. E. O. Saphire, P. W. H. I. Parren, R. Pantophlet, M. B. Zwick, G. M. Morris, P. M. Rudd, R. A. Dwek, R. L. Stanfield, D. R. Burton, and I. A. Wilson, Science 293, 1155 (2001).
4 Optoelectronic-VLSI: Device Design, Fabrication, and Performance David V. Plant Department of Electrical and Computer Engineering, McGill University, Montreal, Quebec H3A 2A7
4.1 Introduction This chapter describes design rules, discusses fabrication steps, and highlights the performance of a number of successful Optoelectronic-VLSI devices that have recently been demonstrated. Motivation for this work can be found by examining the Semiconductor Industry Association (SIA) roadmap which suggests that electrical interconnect technology for both on-chip and off-chip communications will be exhausted in the near future [28]. Optically interconnected chips, boards, and backplanes offer a potential solution to this anticipated electrical interconnect bottleneck. In this context there exist various approaches to quantifying the merits of optics versus electronics for distances ranging from millimeters to meters. A common design assumption is that optics provides increased connectivity through parallelism. Specifically, parallel optical interconnects are capable of providing high-bandwidth communication links both within and between high-performance electronic systems. The advantages of optical communications for long-distance interconnects are well known and provide the motivation for modern optical fiber networks. Optics is now challenging copper at shorter and shorter distances. The benefits of optical interconnects include reduced signal distortion and attenuation, lower power requirements, lighter components, potentially lower costs, and much greater immunity to electromagnetic interference. A thorough review of these physical issues is provided elsewhere [9, 10, 20, 22, 30]. In the commercial arena, several manufacturers now supply optical fiber ribbon-based parallel optical data links (PODLs) of 8 to 12 channels, operating at data rates of up to 3.25 Gb/s per channel over distances of 100–1000 m (depending on bit rate). However, there are applications where many more parallel channels are required and in some cases the interconnect configuration is more complex than a simple 73
74
David V. Plant
point-to-point link. For example, multiprocessor computers, telecommunications switches, and embedded systems all require highly parallel interconnections. In particular, the concept of the direct sourcing and termination of optical signals on silicon has been proposed as a method to relieve the off-chip communication bottleneck [36]. The objective of the approach is to create optical inputs and outputs (I/O) that operate in conjunction with traditional electrical I/O. In recent years, significant progress has been made in the enabling technologies required to achieve this objective. A pivotal step in this evolution includes successful demonstrations of the hybrid integration of Vertical Cavity Surface Emitting Lasers (VCSELs) and PIN photodiodes with Application Specific Integrated Circuits (ASICs) [13, 23, 32]. This emerging technology is now commonly referred to as Optoelectronic-VLSI (OE-VLSI). In this chapter, the author seeks to highlight the significant progress being made in OptoelectronicVLSI technology with a focus on the enabling nanoscale optoelectronic devices and circuits. Much of the reported progress is as a result of a series of successful OE-VLSI ASIC demonstrations. Through the realization of these devices, research in a wide range of areas has been accomplished, including optoelectronic device design, electronic circuit design, and optical design and packaging. This chapter is organized as follows. Section 4.2, OE-VLSI ASIC Design Space, is an overview of key design space criteria. Section 4.3, Heterogeneous Integration, is a description of the key materials parameters and fabrication requirements necessary for realizing OE-VLSI ASICs. Section 4.4, OE-VLSI ASIC Architectures, outlines the options for building these devices. Section 4.5, Enabling Analog Circuit Designs and Performance, summarizes suitable transceiver circuits that have been built using nanoscale CMOS technologies. Concluding remarks are given in Section 3.4.6.
4.2 OE-VLSI ASIC Design Space In developing OE-VLSI technology, several assumptions were made: (1) the optical source is a VCSEL and the detectors are either PN or PIN devices. Most research in this area has been based on the use of devices operating at 850 and 960 nm, although many of the guidelines can be adapted to other wavelengths. (2) Heterogeneous integration using flip-chip bonding and substrate removal of optoelectronic devices onto foundry CMOS ASICS is used. (3) The optical interconnect distance is less than 150 mm (i.e., characteristic of interchip and board-to-board spacing). (4) The optical interconnects could be either fiber based or free-space based. (5) The interconnect is a point-to-point transmissive topology. (6) The interconnect incorporates a realistic tolerance to misalignment. Identification of the design space in which OE-VLSI based chip-to-chip and board-to-board communications using optics was performed. Since the technology is aimed at future high-performance electronic systems, the International Technology Road Map for Semiconductors [28] was consulted. Figure 4.1
4. Optoelectronic-VLSI
75
F i g u r e 4.1. Projected evolution of on-chip clock speed (dashed line, right axis), off-chip clock speed (dotted line, right axis), number of high-speed I/O lines (dash-dot line, left axis), and total bus capacity (solid line, left axis) as a function of time and transistor size for high-performance systems.
shows the projected increase in VLSI transistor on-chip clock speed, off-chip clock speed, number of high-speed off-chip clock lines, and total off-chip I/O capacity as a function of time for high-performance systems, taken from reference [28]. It can be seen that by 2014 the off-chip clock speed is projected to reach 1.8 GHz and the width of the off-chip bus is also projected to increase to 3000 high-speed lines, with a total projected off-chip I/O capacity of 5 Tb/s. The onchip clock speed is projected to reach 13.5 Gb/s. From these data, a view of the design space for off-chip interconnects by the year 2014 was obtained, under the assumption that the necessary off-chip bandwidth will be 5 Tb/s. This is shown in Figure 4.2, where the data rate per channel necessary to achieve 5 Tb/s is plotted as a function of the number of parallel channels. From Figure 4.2, it is apparent that, assuming the optical interconnect channel data rate is not to exceed the projected on-chip data rate of 13.5 Gb/s (which would otherwise require the use of serialization/deserialization circuits), a 5 Tb/s aggregate data rate implies the presence of 370 optical I/Os. Assuming the off-chip optical links run at the projected electrical off-chip clock speed of 1.8 Gb/s implies approximately 2700 optical I/Os would be needed. Let these two values represent the boundaries for optical solutions to the off-chip interconnect problem. To this end, two recently reported OE-VLSI ASICs with 256 optical I/O [23] and 1080 optical I/O[32], respectively, address the required parallelism range. Other researchers have demonstrated matrix addressed VCSEL arrays with 4096 outputs [6]. To illustrate the utility of these OE-VLSI ASICs in an optical interconnect, an example of an experimentally realized point-to-point free-space optical interconnect is shown in Figure 4.3a (Châteauneuf 2002). In this system, two OE-VLSI ASICs were bidirectionally interconnected over a distance of
76
David V. Plant
F i g u r e 4.2. Projected off-chip I/O requirements for 2014.
3 inches. Each chip contains 256 transmitters (VCSELs) and 256 PINs. The interconnection distance was selected such that by inserting two additional prisms into the beam path, it could interconnect two boards in a bookshelf configuration. The relay optics was based on clustered diffractive lenses and the array density of 28 channels/mm2 was achieved. This system represents the highest density free-space interconnect reported to date. A photograph of this system is shown in Figure 4.3b. This system illustrates the necessary components of an optical interconnect, including the ASICs to be interconnected, a PCB (or MCM substrate) on which the ASICs reside, the optical system used for interconnection, and the optical packaging required to realize the link. In designing such a system, some of the OE-VLSI ASIC issues which must be addressed are: materials and integration, CMOS compatibility, transceiver architectures, digital functionality, relay optics, and the various packaging levels, including electrical packaging (which concerns issues such as signal integrity and power dissipation), OE-VLSI ASIC packaging, and optical packaging (which
F i g u r e 4.3. (a) Representative free-space optical interconnect. (b) Photograph of an experimentally realized 512-channel interchip interconnect system.
4. Optoelectronic-VLSI
77
concerns the assembly of the relay optics). Finally, it is necessary to consider the way that these different aspects interact with each other. A key enabler in this technology is the intimate integration of optoelectronic devices with an ASIC substrate. In the following section, methods used for realizing OE-VLSI chips and associated packaging used in system demonstrators are described. For example, the appropriate design guidelines employed in the construction of some specific devices are articulated.
4.3 Heterogeneous Integration Heterogeneous integration is used in order to achieve high density optical I/O. When doing so, it is important to assure compatibility of ASIC metals with the metals used in the flip-chip bump bonding. A related issue is the need to insure alignment of ASIC connection points with III-V device contact points. In the following sections, a heterogeneous integration strategy based on flip-chip bump bonding is summarized. To achieve the OE-VLSI ASICs described, 2D arrays of VCSELs and PDs were fabricated on separate substrates and subsequently integrated onto the ASIC die. In order to support the compact high-density micro-optical interconnects described in Figure 4.3, the VCSELs and PDs were interleaved. The next section describes: the design and target operating properties of the VCSELs and PDs, the OE device layout geometries, and heterogeneous integration techniques including flip-chip bonding and substrate removal of the interdigitated OE devices.
4.3.1 VCSEL and PD Design and Specifications Table 4.1 summarizes the suitable optical and electrical properties of VCSELs and PDs. All property values are measured quantities except those stated as exact numbers, which are quoted from device manufacturer data sheets. As indicated in Table 4.1, the VCSELs used were designed to operate at 850 nm with threshold currents of 1.0 to 4.5 mA and slope efficiencies of 0.25 to 0.35 mW/mA. The devices were also designed to be backside-emitting because of the desire to flipchip bond them to ASIC driver circuits, as described below. This necessitated removal of the GaAs substrate to minimize absorption of light. To achieve these objectives, VCSELs were fabricated with both the n contact and the p contact located on the top surface of the wafer to facilitate electrical contact to the ASIC circuits. Figure 4.4 shows a schematic of the VCSEL geometry indicating emission direction after substrate removal and integration to the ASIC. The p contact was formed above the top distributed Bragg mirror (DBR) and the n contact was brought to the substrate surface through mesa isolation and ion implantation. Figure 4.5 is a photomicrograph of a 2 × 2 VCSEL subarray before flip-chip bump bonding to a CMOS ASIC. The p and n contacts are indicated. The p and n contacts and the VCSEL active area are on a 125-m horizontal
78
David V. Plant T a b l e 4.1. PD and VCSEL optical and electrical properities PD parameter
Symbol
Responsivity Junction capacitance Dark current
R CJ Idark
VCSEL parameter
Symbol ITH 25 C 25 C ITH T T R2−5mA VTH 2mA CJ
Threshold current (@25 C) Slope efficiency (@25 C) ITH temperature dependence temperature dependence Differential resistance (2-5 mA) Threshold voltage (@2mA) Junction capacitance
Value 0317A/W ± 108 mA/W 500 fF 6 nA
Value 1400 mA ± 75 A 0340 W/A ± 10 mW/A 151 A C −22 mW/A C 717 ± 121 1580V ± 17mV 500 fF
and vertical pitch. Once bonded to the ASIC as per the description given below, the n contact and the DBR becomes the top (emitting) surface of the VCSEL. The PDs were fabricated with square active areas of 50 m on a side and 15 × 15 m pads for the p and n contacts. The PD active areas were placed on a 125-m vertical pitch. Figure 4.6 is a photograph of a 2 × 2 PD subarray before flip-chip bump bonding to a CMOS ASIC. The p and n contacts and a unit cell are indicated.
4.3.2 Heterogeneous Integration and Substrate Removal The VCSELs and PDs were integrated onto the CMOS drivers using flipchip bonding and substrate removal techniques. The contact areas on the
pn-contact brought to wafer surface
DB Gain DB nn-type semi insulating VCSEL emission direction post hybridization and substrate
F i g u r e 4.4. Schematic of the VCSEL geometry indicating the emission direction post substrate removal.
4. Optoelectronic-VLSI
79
F i g u r e 4.5. Photomicrograph of a 2x2 VCSEL subarray before after flip-chip bump bonding to a CMOS ASIC. The p and n contacts are indicated. The p and n contacts and the VCSEL active area are on a 125-m horizontal and vertical pitch.
CMOS die for the VCSEL driver and PD receiver were identical to those on the optoelectronic devices. Heterogeneous integration was accomplished by employing relatively conventional photolithographic processes to deposit and lift off contact metals on the wafers followed by a precision assembly process using a flip-chip bonding tool. In the photolithographic step, a photoresist polymer was first spun out on the wafer and printed with the contact metal pattern and then developed. Indium was then evaporated onto the wafer and the photoresist was lifted off, leaving metal on the contact pads. This process was used for the VCSEL and PD wafers and the CMOS dies. The individual OE device dies were separated by mechanical dicing and then integrated onto a CMOS die using the precision alignment hybridization tool. The VCSEL die was first attached to the CMOS chip followed by dry etching to remove the substrate; integration of the PD die was accomplished next followed by substrate removal. The bonding of the indium metal contacts on the CMOS chip and on the OE devices was accomplished through a combination of force and controlled temperature. In summary, the process resulted in electrical isolation of individual OE devices and allowed the interleaving of the VCSEL and PD devices onto a single CMOS die. Although individual dies were used to assemble this generation of OE-VLSI ASICs, migration of the process to the wafer level is relatively straightforward. The above process was found to be very effective in realizing the OE-VLSI ASICS used in the systems to date. As suggested, the process
80
David V. Plant
F i g u r e 4.6. Photograph of a 2 × 2 PD subarray before flip-chip bump bonding to a CMOS ASIC. The p and n contacts and a unit cell are indicated.
is relatively straightforward and can be extended to wafer-level integration of devices with wafers of OE devices. The process lends itself to high levels of integration, thus permitting large optical I/O counts.
4.4 OE-VLSI ASIC Architectures The architecture of an OE-VLSI ASIC largely determines the efficiency with which a specific application can be implemented. Determining the appropriate architecture for an application depends on requirements such as the complexity of the processing that must be performed on data or the size of the data set to be operated on. Each architecture type has strengths and weaknesses in terms of compatibility with automated place and route software tools used to realize the ASIC. The three major architectures that have been employed in the design of OE-VLSI ASICs are the pixelized architecture, the modular architecture, and the area-distributed optical padframe architecture [11]. The first two are discussed in the next two sections, through examples of specific OE-VLSI ASICs.
4.4.1 Pixelized/Smart Pixel Architecture The pixelized or smart pixel architecture is based on the development of a self contained unit cell comprised of an optical transmitter, optical receiver, and
4. Optoelectronic-VLSI
81
processing electronics that operate on the locally available data. Each unit cell is self-contained and does not necessarily communicate with other unit cells. The unit cell is tiled to form a 2D array of processing elements as illustrated in Figure 4.7a. The processing complexity that can be implemented in the unit cell is determined by the pitch of the OE Device (OED) arrays used in their construction, and the amount of space occupied by the transmitter and receiver circuits. The pixelized architecture is compatible with applications that involve minimal data processing, such as control and routing functions [23, 24], optical backplanes [19], or multichip interconnection fabrics [7]. It is also compatible with applications that involve large data sets and simple instruction multiple data (SIMD) processing, which is commonly found in image processing applications [17, 21], or in binary neural associative memory applications [5]. The pixelized architecture is not suitable for applications that involve bit-parallel datapath architectures, such as microprocessor and digital signal processing (DSP) cores or random-access memory (RAM), in which highly regular row and column structures are used to achieve timing uniformity and to minimize routing congestion. Adapting these applications to a pixelized architecture would be highly inefficient from a design and layout perspective [11].
F i g u r e 4.7. (a) The unit cell is tiled to form a 2D array of processing elements. (b) A modular layout methodology is shown in which the core processing circuitry and the optical transmitter and receiver arrays are physically separate modules.
82
David V. Plant
The OE-VLSI ASIC required to support the compact point-to-point optical interconnect system described in Figure 4.3 was one employing the pixelized architecture. The interconnect requirements necessitated interleaving the VCSELs and PDs in a clustered geometry as shown in Figure 4.8. VCSELs and PDs were grouped together in clusters such that within each cluster, rows of VCSELs and PDs were interleaved. Resulting clusters consisted of eight VCSELs and eight PDs arranged in four rows. The pitch of the optoelectronic devices was 125 m in both the horizontal and vertical directions; therefore, the VCSELs and PDs were on 125 m horizontal by 250 m vertical pitch. The complete 256-VCSEL and 256-PD array consisted of 32 clusters arranged in eight rows and four columns. The center-to-center spacing of clusters was 750 m horizontally and 750 m vertically. Figure 4.9 is a photograph of the complete OE-VLSI ASIC after VCSEL and PD integration. The CMOS device was a 10-mm × 10-mm chip fabricated in 0.35-m technology with three metal layers. Figure 4.10(a) shows four clusters with 32 VCSELs forward biased (below threshold), and Figure 4.10(b) shows the entire VCSEL array biased above threshold. The distortion seen is caused by the optical system used to image the 3-mm × 6-mm VCSEL array.
F i g u r e 4.8. Four clusters after flip-chip bump bonding and substrate removal. The VCSEL device was 110 m × 1125 m and had a 20-m-diameter active region. The PIN was 125 m by 90 m and had a 50- × 50-m active region.
4. Optoelectronic-VLSI
83
F i g u r e 4.9. Photograph of the complete 256-element VCSEL and PD arrays integrated onto a CMOS ASIC.
4.4.2 Modular Architecture In the design of a large-scale OE-VLSI ASICs, a modular layout methodology as shown in Figure 4.7b has been used, in which the core processing circuitry and the optical transmitter and receiver arrays are physically separate modules that can be separately placed and optimized [11, 32]. Wide and parallel on-chip electrical interconnects are then used to connect the different modules together. The OEDs reside with their respective transmitter and receiver circuits, and the pitch of the OED arrays determines the pitch of the circuits within the transmitter and receiver arrays, and correspondingly the allowed circuit complexity. A limiting
F i g u r e 4.10. (a) Four clusters with 32 VCSELs forward biased (below threshold). (b) The entire VCSEL array biased above threshold. The distortion seen is caused by the optical system used to image the 3-mm × 6-mm VCSEL array.
84
David V. Plant
performance factor for the modular layout methodology is the electrical interconnect used to connect the different modules of the chip. Depending on the physical size of the transmitter and receiver array, these electrical interconnections may be long, and this is of particular concern for the receivers. Buffering circuitry can be used to minimize the latency of driving long on-chip electrical interconnects at a target data rate. Additionally, introducing pipelining stages can be used to shorten the effective latency of long electrical interconnects in synchronous applications that employ the modular architecture [33]. By isolating the digital processing circuitry from the transmitter and receiver arrays, any desired level of processing complexity can be implemented with the modular architecture. The modular architecture has been used in the development of fully interconnected switches [18, 19], a crossbar switch [14], a page buffer chip [11]. an SRAM chip [25], a Fast Fourier Transformer [25], and a multiapplication chip that includes first in, first out (FIFO) buffers, pseudorandom bit sequence (PRBS) data generation, and forward error correction [32]. A photograph of the multi application chip [32] is shown in Figure 4.11 and highlights the principal sections: receiver array, digital section, and transmitter array. The 146-mm × 75-mm chip was built in a 0.25-m, five-metal, singlepoly, n-well foundry CMOS process. The VCSELs and PD were arranged in a 250-m × 250-m grid having 34 rows and 35 columns each. Of the 1190 devices in each OED array, 1080 were used with transmitter or receiver circuits. The remaining 110 OEDs in each array were physically present but not electrically connected to transceiver circuits.
F i g u r e 4.11. Photograph of the chip after flip-chip bump bonding of optoelectronic devices to an underlying CMOS device. The principal sections are shown: receiver array, digital section, and transmitter array.
4. Optoelectronic-VLSI
85
4.5 Enabling Analog Circuit Designs and Performance There are numerous possibilities with respect to transceiver design for OE-VLSI technology. Both single ended and differential designs have been employed. In the following section, both topologies are described including the merits of each. The discussion is partitioned into laser drivers and receivers.
4.5.1 Laser Drivers This subsection presents an optical transmitter based on a low-cost 180-nm CMOS driver and an 850-nm VCSEL operating at 5 Gbps with a total power consumption of 18.35 mW [29]. A detailed bias-dependent modeling approach is used for the VCSEL and an original dual-power rail layout for reduced power consumption is introduced. A description of the simulation bench and test setup is included. The lowest reported power consumption per bandwidth in 180-nm CMOS, of 3.67 mW/Gbps, is achieved with an optical modulation amplitude (OMA) of 3 dBm. This subsection is organized as follows. The design and implementation of the optical transmitter are first outlined. Architectural design decisions are summarized, followed by a unique VCSEL modeling approach based on experimental data. The optical transmitter design, simulation, and implementation are then described. Finally, the test setup and measured optical transmitter performance are presented. 4.5.1.1 Architecture Since applications with potentially wide deployment are contemplated, low manufacturing and operating costs are key drivers. By combining a 180-nm CMOS transmitter (TX) with an 850-nm VCSEL die, minimizing manufacturing costs was sought. In addition, CMOS is ideal for integrating digital processing functions with the transmitter on the same die, further reducing costs. Chip area utilization was minimized for the same reason, but also to fit parallel applications where VCSEL arrays have pitches equaling 125–250 m [34]. As a result, on-chip inductors and cib-ohm resistors were avoided. Minimizing costs also implies minimizing power consumption. This was accomplished by proposing a novel double power-rail ring layout, which will be outlined later in this section. A compact three-stage transmitter architecture is used to keep power requirements low, below the target of 20 mW. As will be shown below, this yields the highest data rate over power consumption ratio reported to date in a 180-nm CMOS. Finally, high data rate and noise robustness influenced most of the architectural design decisions. Maximum performance was achieved through the use of NMOS-based circuits wherever possible. Because PMOS devices are much slower than NMOS transistors, they were used exclusively as loads. In addition, a detailed transition frequency (fT ) analysis was conducted on the available technology to determine the optimum performance bias point. Although this analysis generally applies to small-signal circuits, operating near fT at DC
86
David V. Plant
insured operation in a region of optimum performance. Electrically differential signaling was used to increase the noise robustness of the transmitter. In addition, a current-steering driver was used. This topology generates much less switching noise than a current-switching driver [34]. 4.5.1.2 VCSEL and Other Models Accurate electrical simulations required a good VCSEL model. Reflection parameter (S11) measurements were conducted on several Emcore Gigalase™ VCSEL dies using a radio-frequency (RF) probing station at four different bias currents. The measured S11 curves at the four bias currents for three different dies are given in Figure 4.12. In addition, the differential resistance around the four bias conditions was calculated from the V –I curves. The 2-mA bias current model was used for simulations of the optical transmitter design. An electrical model topology derived from common approaches was used and is shown in Figure 4.13 [3, 35]. The VCSEL model parameters embody pad (RP, CP), junction (RJ, CJ), and mirror (RN, RM) characteristics. Measurements were imported in an Agilent ADS program and model parameters were fitted to the measured S11 and differential resistance independently for the four bias conditions. Optimization of the model parameters was conducted using both random and quasi-Newton search methods with the least-squares error function. The differential resistance at the four bias conditions, compared to the measured values, is given in Table 4.2. Excellent agreement between the measured and
F i g u r e 4.12. Experimental and modeled reflection parameter curves at four bias current levels.
4. Optoelectronic-VLSI
87
F i g u r e 4.13. VCSEL electrical model topology. T a b l e 4.2. Experimental and modeled VCSEL differential resistance at four bias current levels Bias current (mA)
2 4 6 8
RDC Experimental ()
Modeled ()
1034 833 731 670
1040 830 730 670
modeled data is demonstrated. Additional models for the bond wires, test fixture, and package were included in a system simulation bench in Cadence Virtuoso™ with the extracted transmitter layout. 4.5.1.3 Three-Stage Transmitter Design, Implementation, and Simulation A three-stage optical transmitter was used and it is illustrated in Figure 4.14 [27]. It comprises a differential preamplifier, a pulse-shaping stage, and a currentsteering driver. The preamplifier was implemented as a common-gate differential stage, with a 100- matching resistance between its inputs. A 0.4-V low-voltage differential signal (LVDS) is fed to the inputs and amplified near the VDD (1.8 V) and ground rails. The gain of the preamplifier stage is 11 dB and the 3-dB bandwidth for such an input signal is 6 GHz. The pulse-shaping stage is designed as a variable-bias common-source differential pair. The bias of the pulse-shaping stage is varied to adjust the low voltage presented to the current driver. By presenting a low voltage at the current driver inputs that is slightly higher than VX (see Figure 4.14), ringing at the output of the driver stage is significantly reduced [26]. This dynamic adjustment makes it possible to use a wide variety of modulation currents without degradation in performance. The current driver steers a modulation current adjustable in the range 0–4 mA between its two differential pair branches. A bias current source is also included
88
David V. Plant
F i g u r e 4.14. Three-stage optical transmitter schematic.
on-chip and is adjustable between 0 and 8 mA. As an optically single-ended approach was used, a dummy load mimicking the electrical behavior of a VCSEL was implemented in one branch as diode-connected PMOS transistors. Since the VCSEL forward voltage of 2 V is higher than VDD, the VCSEL was connected to a second power rail VCC of 3.3 V. Having the entire optical transmitter connected to VCC is the common approach [16]. On the other hand, this significantly increases power consumption and reduces performance since thick oxide transistors must be used. A dual power rail layout was used where the two are implemented as rings around the die separated by a ground ring. The exterior ring is VCC and brings power to the VCSEL die exclusively. This original approach led to very low power consumption numbers. Having different power supplies for the two branches of the current-steering driver can induce additional switching noise on the power rails. This unbalance was mitigated by laying out a large coupling capacitor on-chip to increase the quality of the local power rails. The optical transmitter extracted layout, combined with the VCSEL and test fixture models, was simulated with SpectreS at 55 C. As the VCSEL is to be uncooled during experiments, it is reasonable to assume the temperature of the CMOS and laser will rise significantly above room temperature. Simulations and experimental measurements showed that the test fixture used was too slow for operation above 2.5 Gbps. As a result, the LVDS inputs are applied directly to the TX inputs through an ideal 50- transmission line. This represents an experimental setup where the input pads are directly probed with 50- highspeed probes. A 210 -1 pseudo-random bit sequence (PRBS) was used to obtain simulated eye diagrams at 2.5 and 5 Gbps shown in Figure 4.15. A modulation
4. Optoelectronic-VLSI
89
F i g u r e 4.15. Simulated eye diagram at (a) 2.5 Gbps and (b) 5 Gbps.
current of 4 mA was applied to the VCSEL model, over a bias current of 2 mA. The threshold current and slope efficiency of the VCSEL are respectively 1 mA and 0.5 mW/mA. Current rise and fall times are 120 and 110 ps at 5 Gbps. The total simulated power consumption from the two voltage rails equals 21.75 mW, including 16.8 mW from the VCSEL modulation and bias currents. The power consumption due to the input ports is negligible. 4.5.1.4 Test Setup and Measured Performance The optical TX die was fabricated by Taiwan Semiconductor Manufacturing Corporation (TSMC) through the Canadian Microelectronics Corporation. It was packaged with the Emcore VCSEL singlet in an 80-pin ceramic quad-flat package (CQFP) and mounted on a printed-circuit board (PCB). The PCB supplied power
90
David V. Plant
and control voltages to the TX while the inputs were fed to the die using 50- Cascade coplanar microprobes. The two wirebonds connecting the VCSEL to the TX die were kept very short (200 m) for maximum performance. A large number of power rail bond wires were used to increase the quality of the on-chip voltage rails by minimizing bond wire equivalent resistance and inductance. The output optical signal was collected by butt-coupling a 50-m core multimode optical fiber to the VCSEL aperture. The signal was converted using a New Focus 12-GHz photoreceiver and analyzed with a Tektronix communication signal analyzer. The LVDS 0.4-V input signals were generated by an Anritsu 12.5-Gbps pattern generator in the form of PRBS of various lengths. The measured eye diagrams at four data rates and a constant PRBS length of 231 -1 are shown in Figure 4.16. The rise and fall times are 180 and 160 ps at 3.125 Gbps. The signal swing of 150 mV is sufficient to directly measure biterror rates (BER) with an Anritsu error detector. With a 3.5-mA modulation current swing, the optical setup efficiency is approximately 66%, for an optical loss of 1.76 dB. The average optical output power is 2 mW. The BER was measured at multiple PRBS lengths and data rates. The results are summarized in Table 4.3. Errorless operation is achieved at a 3.125 Gbps data rate. A BER of 1 × 10−10 is still achieved with a maximum length PRBS at 4 Gbps. This essentially results in error-free operation for a forward-error corrected channel. Performance steadily degrades as the data rate is increased. Although data can be recovered at 5 Gbps, BER performance is insufficient for most applications. The power consumption, which is independent of the data rate due to the analog nature of the optical transmitter, was measured with precision multimeters as the
F i g u r e 4.16. Measured eye diagram after transmission and conversion at (a) 2.5 Gbps, (b) 3.125 Gbps, (c) 4 Gbps, and (d) 5 Gbps.
4. Optoelectronic-VLSI
91
T a b l e 4.3. Measured BER at various data rates and PRBS lengths Data rate (Gbps)
PRBS length
Bit-error rate
1.250 2.500 3.125 4.000 4.000 4.000 5.000 5.000
231 -1 231 -1 231 -1 231 -1 215 -1 27 -1 215 -1 27 -1
Error free Error free Error free